Abstract:Carbon/carbon (C/C) composites are promising structural materials for molten salt reactors (MSRs) because of their exceptional high-temperature performance, resistance to fluoride salt corrosion, and low-neutron-absorption cross-section. However, fluoride salts can infiltrate the pores of C/C composites, potentially causing local hotspots and accelerating material degradation. In this study, a novel C/C composite was fabricated from mesophase–pitch-based carbon fibers and a pitch-based carbon matrix via hot isostatic pressing (HIP). To evaluate its performance under MSR conditions, the composite was exposed to molten FLiBe salt at 700°C and 2–9 atm for a duration of 20 h. Weight gain, morphological characteristics, and crystallinity were characterized after the salt infiltration test. Compared with C/C composites fabricated via conventional chemical vapor infiltration (CVI), the HIP-C/C composite exhibited much better molten salt barrier properties owing to its compact structure and small pore diameter. The weight gain of the HIP-C/C composite was only 0.17 wt.% under 5 atm, significantly lower than the critical index proposed for carbon materials used in MSR. Morphological characterization revealed that FLiBe salt particles were rarely trapped in the small pores of the HIP-C/C composite. While the crystallinity of the salt-impregnated CVI-C/C composite increased, the HIP-C/C composite exhibited a slightly decreased degree of graphitization after salt infiltration. These findings provide insights into the design of high-performance C/C composites for applications in MSR systems.

High temperature in-situ synchrotron-based XRD study on the crystal structure evolution of C/C composite impregnated by FLiNaK molten salt

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Exploring Cr and Molten Salt Interfacial Interaction for Molten Salt Applications

Fabrication and Thermal Conductivity Improvement of Novel Composite Adsorbents Adding with Nanoparticles

Superior molten FLiBe salt barrier properties of a mesophase–pitch-based carbon/carbon composite prepared via hot isostatic pressing

Structural characteristics and ablative behavior of YF 3 modified C/C-ZrC-SiC composites and their preparation by molten salt assisted reactive melt infiltration

The Effect of Molten Salt Infiltration on 2D SiCf/SiC Composite by Chemical Vapour Infiltration

Influence of SiC content in B4C–nSiC composites corrosion in molten FLiNaK salt at 800°C

Salt-Mediated Coarsening in Conversion-Reaction-Synthesized Nanoporous Metals and Nanocomposites Resolved through In Situ Synchrotron Diffraction Studies

Residual stress variation in SiCf/SiC composite during heat treatment and its effects on mechanical behavior

Stress-assisted corrosion behaviour of Hastelloy N in FLiNaK molten salt environment

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

Improvement of curing efficiency and heat resistance of CFRP by the growth of SiCNWs on CF

Molten salt synthesis of Cr3C2-coated flake graphite and its effect on the physical properties of low-carbon MgO–C refractories

Mechanical and thermal properties of in situ AlN/Al-12Si composite fabricated by laser powder bed fusion

In situ infiltration behavior and interfacial microstructure evolution between Al and carbon fibers

Computational Study of the Physical Properties of a High Temperature Molten Salt Mixture of FLiNaK and CeF3

[ICAPP 2023] thermal dehydration tests of FLiNaK salt suitable for thermal-hydraulic experiments

High-quality SiC-HfC coating with interpenetrating structure based on a two-step low temperature molten salt method