Molten salts synthesis of Mo 2 C nanoflake and its composites for enhanced lithium-storage performance

Zheng-Hua He,Jian-Fei Gao,Ling-Bin Kong

DOI: https://doi.org/10.2139/ssrn.4525245

IF: 6.7

2023-10-07

Applied Surface Science

Abstract:The rational design of negative and positive materials to make them have satisfactory specific capacity and rate capability is an effective strategy to enhance the electrochemical properties of Lithium-ion hybrid capacitors (LIHCs). Herein, hierarchical MC-X (X = 0, 1, 2, 3) nanosheet composites were prepared by salt template-assisted solid-state synthesis strategy. Among them, Mo 2 C nanosheets are more dispersed on the amorphous carbon, and the close contact between them makes molybdenum carbide have enough buffer space during the intercalation and deintercalation of Li + , and makes MC-2 have a desirable specific surface area (SSA) of 341.1 m 2 /g. Electrochemical tests showed that the specific capacity of Mo 2 C remained at 313 mAh/g after 1000 cycles at 0.1 A/g, respectively. Meanwhile, the badam shell biochar (B) was prepared by KOH activation. The best sample (B-3) exhibited a high SSA of 3729.969 m 2 /g and high specific capacities of 265.6 mAh/g at 0.1 A/g, respectively. Furthermore, the constructed MC-2//B-3 LIHC exhibits high power density (4.68 kW kg −1 ), energy density (81.19 Wh kg −1 ), and excellent long-cycle stability. Therefore, the key to building a desirable property LIHC is to give consideration to the electrochemical performance between the positive and negative electrodes.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films