Abstract:With the depletion of high-quality ore resources at home and abroad, the supply of domestic coking coal resources has become increasingly tense, and research on the non-blast furnace ironmaking technology has become even more necessary. The fluidized ironmaking technology can directly utilize powder ore, does not need to consume coke, and has good prospects for development. However, the sticking problem limits the fluidized ironmaking technology. Therefore, the sticking mechanism of particles must be explored, and inhibition measures must be put forward. Although many researchers at home and abroad have performed numerous studies on the influencing factors and inhibiting technologies of the sticking problem, the quantitative characterization and analysis of the sticking degree have rarely been studied. Similar to the fluid viscosity, the apparent viscosity of solid particles was introduced herein to characterize the interaction force between particles. The apparent viscosity of Fe2O3 particles with nano-SiO2 were measured by a rotational viscometer based on the principle of energy dissipation. The results indicate that the apparent viscosity of Fe2O3 particles increases with the increasing temperature and significantly decreases when nano-SiO2 is added. This result could be explained by the nanoSiO 2 coating on the particles inhibiting the agglomeration and sintering among particles. Sticking occurred during the fluidization process. The reduction of Fe2O3 particles was investigated by a micro-fluidized bed to verify the effect of nano-SiO2 on the apparent viscosity of Fe2O3 particles. Consequently, the results show that adding nano-SiO2 to the Fe2O3 particles can effectively improve the metallization rate and prolong the sticking time in the reduction process. Furthermore, the scanning electron microscopy analysis exhibits that the nano-SiO 2 coating on Fe2O3 particles reduces the diffusion activity of the iron atoms, blocks the contact between fresh iron, and inhibits the sintering of fresh iron, thereby making it difficult to form sticking points. In conclusion, adding nano-SiO2 to Fe2O3 particles can effectively inhibit sticking in the reduction process of the fluidized bed.

Improvement on fluidization and reduction of ultrafine CuO powders with the assistance of iron microspheres

SiO 2 microsphere-assisted reduction of ultrafine CuO powder in a fluidized bed

Effect of High Temperature Reduction Process on Compressibility of Water-Atomized Iron Powder

Influence of mixing inside microreactor on microstructural evolution of Cu-ZnO catalyst

The Effect of Mixing on Co‐precipitation and Evolution of Microstructure of Cu‐ZnO Catalyst

Reduction reaction in Al-CuO powder mixture driven by mechanical alloying

Enhancing Zero-Valent Iron (ZVI) Pulverization During Mechanical Milling: FeSx As Milling Aids

Synthesis of uniform LiZnTi ferrite with enhanced magnetic properties through CuO nanoparticle substitution

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Synthesis of Ultra-Fine Iron Powder by Combining the Flame Aerosol Synthesis and Postreduction

Influence of Ferric Oxide Modification on the Properties of Copper Oxide Supported on Γ-Alumina

Effect of temperature and reaction path interaction on fluidization reduction kinetics of iron ore powder

Effect of Nano-Sio2 Addition on the Apparent Viscosity of Fe2O3 Particles

Diameter and Aggregation Controlled Preparation by Solvothermal Synthesis of Ultra-small Particles CuFe$_2$O$_4$

Effect of different modification methods on fluidized bed hydrogen reduction of cohesive iron ore fines

The coprecipitation formation study of iron oxide nanoparticles with the assist of a gas/liquid mixed phase fluidic reactor

Effect of reaction condition on microstructure and properties of (NiCuZn)Fe2O4 nanoparticles synthesized via co-precipitation with ultrasonic irradiation

Enhancing flotation separation of fine copper oxide from silica by microbubble assisted hydrophobic aggregation

Influence of Cu on the Improvement of Magnetic Properties and Structure of L10 FePt Nanoparticles

Ultrasonic-assisted Preparation of Monodisperse Iron Oxide Nanoparticles