Abstract:The reduction of Fe-based nanocomposite catalysts doped with Al and Cu has been studied using in situ X-ray diffraction (XRD), in situ X-ray absorption near-edge structure (XANES), and temperature-programmed reduction (TPR) techniques. The catalysts have been synthesized by melting of iron, aluminum, and copper salts. According to XRD, the catalysts consist mainly of Fe2O3 and Al2O3 phases. Alumina is in an amorphous state, whereas iron oxide forms nanoparticles with the protohematite structure. The Al3+ cations are partially dissolved in the Fe2O3 lattice. Due to strong alumina-iron oxide interaction, the specific surface area of the catalysts increases significantly. TPR and XANES data indicate that copper forms highly dispersed surface CuO nanoparticles and partially dissolves in iron oxide. It has been shown that the reduction of iron(III) oxide by CO proceeds via two routes: a direct two-stage reduction of iron(III) oxide to metal (Fe2O3 → Fe3O4 → Fe) or an indirect three-stage reduction with the formation of FeO intermediate phases (Fe2O3 → Fe3O4 → FeO → Fe). The introduction of Al into Fe2O3 leads to a decrease in the rate for all reduction steps. In addition, the introduction of Al stabilizes small Fe3O4 particles and prevents further sintering of the iron oxide. The mechanism of stabilization is associated with the formation of Fe3- xAl xO4 solid solution. The addition of copper to the Fe-Al catalyst leads to the formation of highly dispersed CuO particles on the catalyst surface and a mixed oxide with a spinel-type crystalline structure similar to that of CuFe2O4. The low-temperature reduction of Cu2+ to Cu0 accelerates the Fe2O3 → Fe3O4 and FeO → Fe transformations but does not affect the Fe3O4 → FeO/Fe stages. These changes in the reduction properties significantly affect the catalytic performance of the Fe-based nanocomposite catalysts in the low-temperature oxidation of CO.

Influence of Ferric Oxide Modification on the Properties of Copper Oxide Supported on Γ-Alumina

The Influence of Cu and Al Additives on Reduction of Iron(III) Oxide: In Situ XRD and XANES Study.

Influence of magnesia modification on the properties of copper oxide supported on γ-alumina

Influence of Calcination Temperature on the Dispersion Behavior and CO Oxidation Properties of CuO/γ-Al<SUB>2</SUB>O<SUB>3</SUB> Catalyst: Influence of Calcination Temperature on the Dispersion Behavior and CO Oxidation Properties of CuO/γ-Al<SUB>2</SUB>O<SUB>3</SUB> Catalyst

Influence Of Calcination Temperature On The Dispersion Behavior And Co Oxidation Properties Of Cuo/Gamma-Al2o3 Catalyst

The Strong Promoting Effects of Thin Layer Al2O3 on FeCu Fenton-like Components: Enhanced Electron Transfer.

Influence of Titanium Oxide on the Surface Interactions of MO (m=cu and Ni)/γ-Al2O3 Catalysts

Dispersion of Fe2O3 supported on metal oxides studied by Mössbauer spectroscopy and XRD

Surface Interaction Between Copper Oxide and CeO2-γ-Al2O3 Mixed Oxide Support

CO Oxidation over Alumina-Supported Copper Catalysts

Preparation,Characterization and Catalytic Performance of CuO/Mn_2O_3/γ-Al_2O_3 Catalysts over CO Oxidation

Preparation, Characterization and Catalytic Performance of CuO/Mn2O3/gamma-Al2O3 Catalysts over CO Oxidation

Reduction of Supported Iron Oxide Studied by Temperature-Programmed Reduction Combined with Mössbauer Spectroscopy and X-ray Diffraction

High activity of CuO/#-Fe2O3 for low temperature CO oxidation: Effect of support crystal types in catalyst design

Dispersion and Physico-Chemical Characterization of Iron Oxide on Various Supports

Characterization of Dispersion and Surface States of NiO/γ-alumina and NiO/La2O3–γ-alumina Catalysts

Activities Of Mo(M=Cu And Ni)/Tio2/Gamma-Al2o3 Catalysts In Co Oxidation

Enhancing the Fenton-like reactions performance of copper-iron oxide by inducing a lower valence state using oxidized g-C 3 N 4 support

A monolayer dispersion study of titania-supported copper oxide

Surface Structure Characteristics of CuO/Ti0.5Sn0.5O2 and Its Activity for CO Oxidation

Surface Hydroxyl-Determined Migration and Anchoring of Silver on Alumina in Oxidative Redispersion