Abstract:Nanocrystalline diamond (NCD) films are attractive for many applications due to their smooth surfaces while holding the properties of diamond. However, their growth rate is generally low using common Ar/CH4 with or without H2 chemistry and strongly dependent on the overall growth conditions using microwave plasma chemical vapor deposition (MPCVD). In this work, incorporating a small amount of N2 and O2 additives into CH4/H2 chemistry offered a much higher growth rate of NCD films, which is promising for some applications. Several novel series of experiments were designed and conducted to tailor the growth features of NCD films by fine-tuning of the gas-phase compositions with different amounts of nitrogen and oxygen addition into CH4/H2 gas mixtures. The influence of growth parameters, such as the absolute amount and their relative ratios of O2 and N2 additives; substrate temperature, which was adjusted by two ways and inferred by simulation; and microwave power on NCD formation, was investigated. Short and long deposition runs were carried out to study surface structural evolution with time under identical growth conditions. The morphology, crystalline and optical quality, orientation, and texture of the NCD samples were characterized and analyzed. A variety of NCD films of high average growth rates ranging from 2.1 μm/h up to 6.7 μm/h were successfully achieved by slightly adjusting the O2/CH4 amounts from 6.25% to 18.75%, while that of N2 was kept constant. The results clearly show that the beneficial use of fine-tuning of gas-phase compositions offers a simple and effective way to tailor the growth characteristics and physical properties of NCD films for optimizing the growth conditions to envisage some specific applications.

Growth rate and EBSD texture analysis of nitrogen doped diamond films

Effect of Nitrogen on Growth and Optical Properties of Single-Crystal Diamond Synthesized by Chemical Vapor Deposition

Structure and Mechanical Performance of Nitrogen Doped Diamond-like Carbon Films

High nitrogen amounts incorporated diamond films deposited by the addition of nitrogen in a hot-filament CVD system

Influence of CVD diamond growth conditions on nitrogen incorporation

The influence of nitrogen and oxygen on the high nucleation density diamond growth

The Structural Evolution Of Nanocrystalline Diamond Films Synthesized By R.F. Pecvd

Effects of Nitrogen on Formation and Properties of Diamondlike Films Synthesized by Dual Ion Beam Deposition

A Study of the affect of N and B doping on the growth of CVD diamond (100):H 2 X 1 surfaces

Structural and optical characterizations of nanostructured diamond films grown on Si(001) substrates

Investigation of carbon nitride films by cathodic arc evaporation

Characterization of Nitrogen Doped Chemical Vapor Deposited Single Crystal Diamond Before and after High Pressure, High Temperature Annealing

Thin Film Growth Conditions for Cvd Diamond under Low Pressure

The Interface and Mechanical Properties of a CVD Single Crystal Diamond Produced by Multilayered Nitrogen Doping Epitaxial Growth

Effect of Nitrogen on Deposition and Field Emission Properties of Boron-Doped Micro- and Nano-Crystalline Diamond Films

Tailoring of Nitrogen-Vacancy Colour Centers in Diamond Epilayers by in Situ Sulfur and Nitrogen Anion Engineering

Growth Morphology of Boron Doped Single Crystal Diamond

Doping of rf plasma deposited diamond-like carbon films

Nitrogen overgrowth as a catalytic mechanism during diamond chemical vapour deposition

Fast, Efficient Tailoring Growth of Nanocrystalline Diamond Films by Fine-Tuning of Gas-Phase Composition Using Microwave Plasma Chemical Vapor Deposition

NV-doped microstructures with preferential orientation by growth on heteroepitaxial diamond