Interfacial microstructure, mechanical properties and strengthening mechanism of Mg/Al bimetallic composites produced by a novel compound casting with the addition of Gd

Feng Guan,Wenming Jiang,Zheng Zhang,Junlong Wang,Guangyu Li,Zitian Fan
DOI: https://doi.org/10.1016/j.matchar.2023.112898
IF: 4.537
2023-04-13
Materials Characterization
Abstract:To strengthen the bonding properties of Mg/Al bimetallic composites, rare earth Gd was added to the Mg/Al bimetallic composites manufactured by a novel compound casting, and the interfacial microstructure, mechanical properties and strengthening mechanism of the Mg/Al bimetallic composites with Gd addition were studied. Without Gd addition, there was a thin oxide film consisting of an alumina phase in the Mg/Al bimetallic interface, which hindered the diffusion of Mg 2 Si phase. After adding the Gd, the oxide film in the interface was broken and dissolved, significantly increasing the diffusion distance of the Mg 2 Si phase. The Al 2 Gd and Al 8 Mn 4 Gd precipitated in the interface. However, with the increase of the Gd content, the distribution of the Gd precipitates gradually became inhomogeneous. The primary Al 12 Mg 17 phase and eutectic structure in the interface were greatly refined due to the heterogeneous nucleation and the inhibition of growth caused by the Mg 2 Si phase and Gd-rich precipitates. The interface was strengthened under the comprehensive effect of the fine grain strengthening and precipitation strengthening of the Mg 2 Si and Gd-rich precipitates. When the Gd content increased to 0.6 wt%, the shear strength of the Mg/Al bimetallic composites reached the maximum of 46 MPa, which was 39% higher than that of the bimetallic composite without Gd addition. With the further increase of the Gd content, the aggregation of the Gd-rich precipitates and the excessive thickness of the interface led to the decrease of the shear strength of the Mg/Al bimetallic composites.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?
This paper aims to solve the problems in the interface bonding performance of Mg/Al bimetallic composites. Specifically, the authors added the rare - earth element Gd to Mg/Al bimetallic composites and prepared these composites by using a new composite casting technology, and studied the influence of the addition of Gd on the interface microstructure, mechanical properties and strengthening mechanism of Mg/Al bimetallic composites. ### Main Problems and Solutions 1. **Oxide Film Hindering Diffusion**: - **Problem**: When Gd was not added, there was a thin oxide film composed of aluminum oxide at the Mg/Al bimetallic interface, and this oxide film hindered the diffusion of the Mg₂Si phase. - **Solution**: After adding Gd, the oxide film at the interface was broken and dissolved, significantly increasing the diffusion distance of the Mg₂Si phase. 2. **Interface Microstructure Optimization**: - **Problem**: The interface microstructure of Mg/Al bimetallic composites was relatively rough, which affected the overall performance of the material. - **Solution**: The addition of Gd promoted heterogeneous nucleation and growth inhibition, significantly refining the primary Al₁₂Mg₁₇ phase and eutectic structure at the interface. 3. **Mechanical Property Improvement**: - **Problem**: The shear strength of Mg/Al bimetallic composites was low. - **Solution**: The addition of Gd significantly increased the shear strength of the interface through the combined effect of grain refinement strengthening and precipitation strengthening. When the Gd content increased to 0.6 wt%, the shear strength of Mg/Al bimetallic composites reached a maximum value of 46 MPa, which was 39% higher than that of the composites without Gd addition. ### Experimental Results and Discussion - **Microstructure Changes**: - After adding Gd, Al₂Gd and Al₈Mn₄Gd precipitation phases were formed at the interface, and these precipitation phases were helpful to improve the mechanical properties of the interface. - As the Gd content increased, the distribution of Gd - rich phases gradually became non - uniform, affecting the interface performance. - **Mechanical Properties**: - The shear strength test results showed that as the Gd content increased, the shear strength of Mg/Al bimetallic composites first increased and then decreased. When the Gd content was 0.6 wt%, the shear strength reached a maximum value of 46 MPa. - When the Gd content was further increased to 0.9 wt%, due to the aggregation of Gd - rich phases and the increase in interface thickness, the shear strength decreased. ### Conclusion By adding an appropriate amount of Gd to Mg/Al bimetallic composites, its interface microstructure and mechanical properties can be significantly improved. However, an excessive amount of Gd will lead to the non - uniform distribution of Gd - rich phases and an increase in interface thickness, thereby reducing the performance of the material. Therefore, the optimal Gd addition amount is 0.6 wt%, at which time the shear strength of the material is the highest.