Abstract:The evolution of the microstructure and mechanical properties of alloy system with nominally composition Mg–5Li–1Zn–0.5Ag–0.5Zr– x Gd ( x = 0, 1.2, 2.4, 3.6, 4.8, 6) is evaluated based on computational phase diagram and corresponding experimental studies. The results show that grains are significantly refined with the increase of Gd content. The main phases of as-cast alloys are α -Mg, β -Li, AgLi 2 Mg, and Mg 3 Gd. With the increase of Gd content, the amounts of Mg 3 Gd phase and β -Li phase have been increased. When the Gd content exceeds 3.6 wt%, Mg 3 Gd phase precipitates in a form of the network at the grain boundaries. The precipitation of β -Li can be attributed to the competitive dissolution of Zn, Gd, and Li in Mg. Meanwhile, γ ′′ is formed after the addition of Gd, which grows and transforms into γ ′ with the increase of Gd content. In solidification process, stacking faults are formed by solid transformation of partial α -Mg and Mg 3 Gd. Eventually, with the synergistic effect of Mg 3 Gd, β -Li, and γ ′′ (or γ ′), as the Gd content increasing, the tensile strength of the alloy first increases, then decreases, and the elongation decreases. When the content of Gd is 4.8 wt%, the ultimate tensile strength and yield strength reach the maximum values of 227 MPa and 139 MPa, and the elongation is 18.1%, respectively.

Improving tensile properties and corrosion resistance of Mg–Zn–Ca–Mn alloy via Gd addition

A good balance between strength and ductility in Mg–Zn–Mn-Gd alloy

Improving the corrosion resistance of MgZn1.2Gd Zr0.18 (x = 0, 0.8, 1.4, 2.0) alloys via Gd additions

Influences of Gd on the Microstructure and Strength of Mg–4.5Zn Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and Mechanical Properties of the Mg–4.5Zn–xGd (x = 0, 2, 3 and 5) Alloys

Enhanced Mechanical Properties and Corrosion Resistance by Minor Gd Alloying with a Hot-Extruded Mg Alloy

Evolutions of Microstructure and Mechanical Properties in Mg–5Li–1Zn–0.5Ag–0.5Zr–xGd Alloy

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Effect of Gd and Zn Additions on Microstructures and Mechanical Properties of Mg-4sm-3nd-Zr Alloy

Influence of Zn on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Simultaneous improvement of strength and ductility by Mn addition in extruded Mg–Gd–Zn alloy

Effect of minor Gd addition on microstructure, mechanical performance, and corrosion behavior of Mg–Y–Gd alloys

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

Effect of Gd on microstructure and stress corrosion cracking of the AZ91‐extruded magnesium alloy

Microstructure of as-cast Mg-4.2Zn-0.8Y (at.%) alloys containing Gd

Local Atomic Structures of Gd and Zn Atoms in Extruded Mg-Gd-Zn Alloys

High-temperature oxidation behavior and corrosion behavior of high strength Mg-xGd alloys with high Gd content

Improving the corrosion resistance of Mg-8Li-3Al-2Zn alloy by combining Gd alloying and hot extrusion

Microstructure and Mechanical Properties of Mg–9Li–3Al–xGd Alloys