Abstract:Here, a new Mg-1Bi-1Mn-0.3Zn (BMZ110, wt%) wrought alloy designed by the dilute addition of Zn subjected to an appropriate extrusion processing that showed an excellent strength-ductility synergy at room temperature. The main results included four aspects as follows: 1) With dilute Zn addition, the as-cast BMZ110 alloy was refined into an approximately equiaxed-grained structure, since the solid solution of Zn provided a relatively high growth restriction factor. 2) The as-extruded BMZ110 alloy exhibited the finer average grain size and weaker basal texture intensity than the as-extruded BM11 alloy without Zn. The co-segregation of Bi and Zn solutes into grain boundaries was observed to impede grain growth during extrusion and further weaken texture intensity. Moreover, Zn atoms incorporated into Mg3Bi2 phases by replacing Bi atoms increasing the nucleation rate of Mg3Bi2 phases and refining their sizes. 3) Compared with the as-extruded BM11 alloy, the as-extruded BMZ110 alloy demonstrated the higher yield strength (~ 283.4 MPa), ultimate strength (~ 366.2 MPa) and elongation-to-failure (~ 26%). The size refinement of grains and second phases contributed to an extra strength increments. Grain boundary segregation enhanced grain boundary cohesion not only reducing the number density of grain boundary cracks, but also activating more slip modes and grain rotation for increasing the ductility. 4) The as-extruded BMZ110 alloy had the higher grain growth resistance than the as-extruded BM11 alloy during annealing. Solute segregation offered an effective obstacle to restrict grain boundary migration enlarging the activation energy (~ 112.2 kJ/mol) and further delaying the grain growth. Therefore, this work will be helpful for the development of new high performance low-alloyed Mg-Bi based wrought alloys to achieve extensive applications in industries.

Simultaneous improvement of strength and ductility by Mn addition in extruded Mg–Gd–Zn alloy

Effect of Mn content on the microstructure and mechanical properties of as-extruded Zn-0.2Mg-Mn (wt%) alloys

Role of Zn addition on the microstructure and tensile property in Mg–Mn–Nd alloys

Effects of the Simultaneous Addition of Gd and Mn on the Microstructures and Mechanical Properties of Mg-Bi Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

A good balance between strength and ductility in Mg–Zn–Mn-Gd alloy

Effects of Sn and Mn Addition on the Microstructure and Mechanical Properties of As-Extruded Mg–2Al–1Zn Alloys

Effect of High Mn Content on Development of Ultra-Fine Grain Extruded Magnesium Alloy

Influence of Zn on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effect of Mn Modification on Microstructure and Mechanical Properties of Magnesium Alloy with Low Gd Content

Influences of Gd on the Microstructure and Strength of Mg–4.5Zn Alloy

Effect of Nd addition on the microstructure and mechanical properties of extruded Mg-Gd-Zr alloy

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

The effects of Ca and Mn on the microstructure, texture and mechanical properties of Mg-4 Zn alloy

Improving Mechanical Properties of Mg-Al-RE Alloys with the Formed Dimples of Al10Mn2RE Particles and Activated Pyramidal Slip with Mn Additions

Investigation on microstructures and mechanical properties of Mg–6Zn–0.5Ce–xMn (x = 0 and 1) wrought magnesium alloys

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Novel Mg-Bi-Mn wrought alloys: The effects of extrusion temperature and Mn addition on their microstructures and mechanical properties

Improving tensile properties and corrosion resistance of Mg–Zn–Ca–Mn alloy via Gd addition

Simultaneous improvement of strength and damping capacity of Mg-Mn alloy by tailoring bimodal grain structure