Effects of Sn and Mn Addition on the Microstructure and Mechanical Properties of As-Extruded Mg–2Al–1Zn Alloys

Fu-Hao Gao,Bin-Jiang Lv,Tie-Wei Xu,Ning Cui,Feng Guo

DOI: https://doi.org/10.1007/s12540-023-01435-5

IF: 3.451

2023-04-12

Metals and Materials International

Abstract:The effects of low Sn (1.0 wt%) and Mn (0.5 wt%) content on the microstructures and mechanical properties of as-extruded Mg–2Al–1Zn (AZ21) alloys were systematically investigated. The combined addition of Sn and Mn significantly refined the grains of the AZ21 alloy, reducing the average grain size from 25.77 to 2.17 μm. The volume fraction of the dynamically recrystallized (DRXed) grains decreased from 78.49 to 43.81% with Sn (1.0 wt%) and Mn (0.5 wt%) addition. The Al 8 Mn 5 , Al 11 Mn 4 , and Al 9 Mn 4 phases were formed in Mg–2Al–1Zn–1Sn–0.5Mn (AZTM2110) alloy, and the Mg 17 Al 12 phase disappeared. The orientation relationship between Al 9 Mn 4 and Al 11 Mn 4 was (002) Al11Mn4 //( 02) Al9Mn4 , [ 00] Al11Mn4 //[223] Al9Mn4 , and the orientation relationship between Al 8 Mn 5 and α-Mg was ( 52) Al8Mn5 //( 2 3) α−Mg . The Al 9 Mn 4 and Al 11 Mn 4 phases grew in the same direction. The intensity of basal fiber texture of AZTM2110 alloy decreased by 21.7%. The ultimate tensile strength, yield strength, and elongation of the AZ21 alloy increased by 29.03%, 65.05%, and 61.02%, respectively. Grain-refinement strengthening was the main mechanism underlying the improvement in AZTM2110 alloy strength. Grain refinement and the weakened basal fiber texture improved the plasticity of the AZTM2110 alloy. Graphical

materials science, multidisciplinary,metallurgy & metallurgical engineering