Abstract:The combined addition of small amounts of Ca and Y to Mg–Al–Zn alloys has recently been found to greatly improve the ignition resistance, corrosion resistance, and mechanical properties of these alloys. However, Mg–Al–Zn–Ca–Y alloys with high Al content show poor extrudability, which is an obstacle to their use as extruded components in industrial applications. This study aims to improve the extrudability of a Mg–Al–Zn–Ca–Y alloy through the addition of a small amount of mischmetal (MM). To this end, a trace amount (0.5 wt%) of Ce-rich MM is added to a Mg–9Al–0.8Zn–0.9Ca–0.6Y (AZXW9110) alloy. MM addition leads to significant grain refinement of the homogenized billet, from 326 to 180 μm. When the MM-added alloy is extruded into a sheet at 350 °C with an extrusion ratio of 22.9, the maximum ram speed at which it is extrudable without the occurrence of hot cracking is 12 mm/s, substantially higher than the 2 mm/s possible without MM addition. The Ce and La atoms decomposed from the MM are dissolved in the Mg17Al12, Al8Mn4Y, Al2Ca, and Al2Y phases, apparently leading to an increase in the thermal stability of the phases and, consequently, to an improvement in the AZXW9110 alloy's extrudability. At ram speeds above 2 mm/s, many small-sized cracks form at the edges of the extruded AZXW9110–0.5MM sheets. As the ram speed increases up to 6 mm/s, the number density of edge cracks gradually increases while their average spacing decreases, but beyond 6 mm/s both remain almost unchanged.<h3 class="a-plus-plus">Graphic </h3>

Refined microstructure and improved mechanical properties of high-ratio extruded AZ91−xSn magnesium alloy

Improvement of mechanical properties of hot extruded and age treated Mg–Zn–Mn–Ca alloy through Sn addition

Effect of Sn Addition on the Microstructure and Mechanical Properties of AZ31 Alloys

Effects of Sn and Mn Addition on the Microstructure and Mechanical Properties of As-Extruded Mg–2Al–1Zn Alloys

Optimizing Superplasticity of AZ91−xSn Magnesium Alloys with Competitive Grain Growth and Boundary Sliding

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Mechanical Properties and Microstructures of Mg-Al-Zn Alloys with High Aluminum Contents

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Effect of Zn Concentration on the Microstructures and Mechanical Properties of Extruded Mg–7Y–4Gd–0.4Zr Alloys

Effects of Zn Addition on the Microstructure, Tensile Properties and Formability of As-Extruded Mg-1Sn-0.5Ca Alloy

Effect of Ca addition on microstructure and mechanical properties of Mg–3.8Al–1.1Sn alloys

Developing a high-speed-extruded BMZQ5100 alloy with higher strength and microstructural thermal stability than AZ91 alloy

Improving mechanical properties of Mg-Sn alloys by co-addition of Li and Al

Enhanced strength-ductility synergy and activation of non-basal slip in as-extruded Mg–Zn–Ca alloy via heterostructure

Effect of Al on the Microstructure and Mechanical Properties of Mg–Sn–Ca–Mn Wrought Alloy

Significant Improvement in Extrudability of Mg–9Al–0.8Zn–0.9Ca–0.6Y Alloy Through Mischmetal Addition

Achieving superior mechanical properties in a low-alloyed magnesium alloy via low-temperature extrusion

Synergistic effects of alloying, homogenization, and hot extrusion on the mechanical properties of as-cast Mg–Al–Ca magnesium alloys

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Enhanced Mechanical Properties and Isotropy of Mg-2Al-0.8Sn Alloy through Ca Addition