Abstract:To enhance the low-temperature plasticity and high-temperature strength of molybdenum alloys, we introduce a method of uniformly dispersing nano-ZrTiO4 particles within and between molybdenum grains. This approach effectively eliminates the formation of hard agglomerations between particles and leads to a further refinement of molybdenum grains. The research employs molecular level solid-liquid doping and subsequent liquid dispersion evaporation techniques to successfully synthesize Mo-ZrTiO4 nano-composite powder following H2 reduction. Subsequently, a novel fine-grained Mo-ZrTiO4 alloy sintered billet is successfully fabricated through cold isostatic pressing and high-temperature sintering. To assess the efficacy of the process, three sets of comparative experiments are designed, each employing different methods. The comparative studies have revealed compelling advantages of the liquid dispersed evaporated fine-grained samples of Mo-ZrTiO4. The key advantages identified are as follows:the samples demonstrate a refined grain size, ranging from 2 mu m to 4 mu m. Within the samples, the nano ZrTiO4 particles have an average size of approximately 200 nm. The density and Vickers hardness of the samples is measured at 10.21 g/cm3 and 268.5 +/- 17HV0.2, respectively. The samples exhibit impressive toughness even at room temperature, notably, the high-temperature compressive strength of these samples surpasses that of the deformed samples reported in previous literature concerning this system. The mechanism of liquid dispersion evaporation method in grain nucleation, growth, and powder drying, reduction, and sintering processes was systematically elaborated. Simultaneously, a detailed analysis was conducted on two high-temperature strengthening mechanisms that impact the mechanical properties. The results indicate that this excellent performance can be attributed to the synergistic effect of both fine grain strengthening and uniform dispersion strengthening of second-phase nanoparticles.

In-situ oxide dispersion strengthened ultrafine-grained molybdenum alloy with enhanced hardness and bending strength

Microstructure, Compressive Performance and Wear Resistance of Pure Molybdenum Additively Manufactured Via Laser Powder Bed Fusion

Microstructure and Mechanical Properties of Unalloyed Molybdenum Fabricated Via Wire Arc Additive Manufacturing

Microstructure and compression properties of fine Al2O3 particles dispersion strengthened molybdenum alloy

Preparation of nanostructural oxide dispersion strengthened (ODS) Mo alloy by mechanical alloying and spark plasma sintering, and its characterization

Mechanical properties and strengthening mechanism of the hydrothermal synthesis of nano-sized α-Al2O3 ceramic particle reinforced molybdenum alloy

Microstructure, Mechanical Properties, and Strengthening Mechanisms of Nanostructural Y-Zr-O Oxide Dispersion-Strengthened (ODS) Mo Alloys

Nanostructured High-Strength Molybdenum Alloys with Unprecedented Tensile Ductility.

Microstructure refinement and second phase particle regulation of Mo−Y2O3 alloys by minor TiC additive

Origin and Formation of Oxygen and Its Effects on Microstructure Evolution and Properties of Molybdenum

Processing Heterogeneously Structured Oxide-Dispersion-strengthened Fe-10Cr-6.1Al-0.3Zr-0.1Y Alloy for Simultaneously Enhanced Strength and Ductility

Strengthening the grain boundary of Mo alloy via little TiC addition

Study on preparation and properties of molybdenum alloys reinforced by nano-sized ZrO 2 particles

Achieving an unprecedented strength-ductility balance of molybdenum alloy by homogeneously distributing yttrium-cerium oxide

Microstructure and high-temperature deformation performance of liquid-dispersed evaporated Nano-ZrTiO4 doping molybdenum alloy

Nano Mo–La–O particles strengthened Mo alloys fabricated via freeze-drying technology and low temperature sintering

Effects of shape and size of second phase on mechanical properties of sintered Mo-Y2O3 alloys

Achieving ultrahigh strength in oxide-dispersion-strengthened CoCrNi alloy via in situ formation of coherent Y-Ti-O nanoprecipitates

Boosted mechanical properties of sintered MoLa alloys with ultrafine-grains by the nanostructuring of secondary phase

Characterization of Al2O3 in High-Strength Mo Alloy Sheets by High-Resolution Transmission Electron Microscopy.

Microstructure and Tensile Properties of Oxide Dispersion Strengthened Molybdenum Alloys Prepared by Different Doping Process