Developing a uniform distribution of bimodal α-Mo grains in the Mo–Si–B alloy for toughness and strength improvement

Juan Wang,Xiaojiao Zhang,Yongkang Zhou,Guojun Zhang,Bin Li,Rui Li,Shujuan Li

DOI: https://doi.org/10.1007/s10853-023-08917-2

IF: 4.5

2023-10-01

Journal of Materials Science

Abstract:Mo-Si-B alloys consisting of α-Mo, Mo 3 Si, and Mo 5 SiB 2 phases have high melting point above 2000 °C and have potential as ultra-high temperature structural materials. However, the room-temperature fracture toughness falls short of meeting the practical application, and enhancing the toughness through grain coarsening inevitably leads to a trade-off with the strength of the Mo–Si–B alloy. Bimodal structure design is expected to improve both the toughness and strength simultaneously. In the present work, Mo–12Si–8.5B alloy with a unique bimodal microstructural design was successfully prepared via multistep mechanical alloying, followed by hot pressing. The bimodal structure comprised fine (~ 0.65 μm) α-Mo grains and partial coarse (~ 1.25 μm) α-Mo grains, which exhibited a uniform distribution and formed a continuous matrix embedded with fine Mo 3 Si and Mo 5 SiB 2 intermetallics. Such microstructure enhanced the fracture toughness and compressive strength simultaneously, exhibiting 14.3 MPa m 1/2 and 3130 MPa, respectively. The coarse α-Mo grains involved increasing dislocation motion and storage capacity, playing an important toughening role as the crack trapper. The uniform distribution of the bimodal α-Mo grains combined with the continuous matrix promoted uniformity of the strain distribution and alleviated the plastic constraint on α-Mo imposed by intermetallics, which then maximized the extent of crack trap toughening of α-Mo. The existence of fine α-Mo grains strengthened the alloy.

materials science, multidisciplinary