Unexpected strengthening of the Mo-containing low-density steel achieved through a novel nano-ordered phase

Yuxiang Liu,Jianlei Zhang,Yunhu Zhang,Gang Chen,Changjiang Song,Qijie Zhai

DOI: https://doi.org/10.1016/j.msea.2024.146159

2024-03-01

Abstract:Mo element has been considered as an effective element to regulate the nano-precipitation behavior in low-density steel. In this work, a novel nano-ordered phase was found in austenite of the Fe–28Mn–10Al-1.2C (wt.%) low-density steels with 3 wt% and 5 wt% Mo addition. HRTEM characterization indicated that this nano-ordered phase had a chemical composition similar to austenite matrix and a L′12 structure similar to κ-carbides. Although the Mo addition suppressed the precipitation and growth of κ-carbides in austenite, the nano-hardness testing showed that the formation of the novel nano-ordered phase caused by Mo addition resulted in a higher hardness of austenite. Based on the tensile property analysis of the Mo-containing steels, although the Mo addition decreased the precipitation strengthening of intragranular κ-carbides, the novel nano-ordered phase resulted in an additional strength contribution of 309 MPa. In addition, the formation of this novel nano-ordered phase had significant improvement on the strain hardening rate. Consequently, the Mo addition simultaneously increased the strength and plasticity of the low-density steels. The novel nano-ordered phase caused by Mo has rarely been reported in literatures, its contribution on the strength and strain hardening ability indicated its potential application in the regulation of mechanical properties.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering