Synergetic effects of complex additions of Mo and Ni on the phase transformation behavior and mechanical properties of austenitic lightweight steels

Joonoh Moon,Seong-Jun Park,Kyeong-Won Kim,Hyun-Uk Hong,Heung Nam Han,Bong Ho Lee
DOI: https://doi.org/10.1002/srin.202200251
IF: 2.1258
2022-09-22
steel research international
Abstract:Fe‐30Mn‐10.5Al‐1.1C alloys with different Mo and Ni contents were prepared to investigate the phase transformation behavior and the mechanical properties of austenitic lightweight steels. Solution‐treated samples had microstructures consisting of an austenite matrix and ordered κ‐carbides, and the size of the κ‐carbides decreased with the addition of Mo or Ni. In addition, the ordered‐BCC phases of B2 and DO3 also formed when 3wt%Mo and 3wt%Ni were complexly added, resulting in a large decrease of the austenite grain size. Nanoindentation experiments showed that the intrinsic strength of the austenite matrix changed depending on the precipitation behavior of the κ‐carbide; i.e. , the addition of 3wt%Mo or 3wt%Ni decreased the intrinsic strength of the austenite by suppressing κ‐carbide precipitation, while complex additions of 3wt%Mo and 3wt%Ni increased them again. The results of tensile tests showed that the alloy containing both 3wt%Mo and 3wt%Ni exhibits the highest yield(1102 MPa) and tensile strength(1155 MPa) with large tensile ductility(33%) due to the effects of grain refinement of the austenite grains and the formation of secondary hard phases of DO3 and B2, as well as κ‐carbides. Finally, the changes in the precipitation behavior of the κ‐carbide were investigated via transmission electron microscopy and atom probe tomography analyses. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?