Abstract:Despite the wealth of literature on the friction and wear behaviour of ceramics, their wear mechanisms are far from well understood. The need to develop a precise understanding of the wear mechanisms is imperative for the development of better wear-resistant ceramics. Particularly in alumina ceramics, grain coarsening has been found to improve the crack growth resistance characteristics. However, if the same would be beneficial for wear resistant applications has not been systematically investigated. To evaluate if there exists a strong grain size effect on abrasive wear mechanisms in ceramics, a series of tests were conducted under severe sliding contact conditions in an alumina ceramic. Unlubricated sliding wear tests were performed on alumina of three different grain sizes, 0.7, 5 and 25 μm, using a blunt conical diamond indenter of about 100-μm tip radius as the slider at room temperature under normal loads of 8–40 N and sliding distances up to 120 mm. The abrasive wear behaviour was characterised by measuring the wear volume and wear rate as a function of normal load and sliding distance. In addition, the friction behaviour was also studied simultaneously as a function of these two variables. The wear damage mechanisms were examined using both optical and electron microscopy as well as energy dispersive X-ray spectroscopy. For a given grain size and sliding distance, the width and depth of the worn track (hence wear volume) and the frictional force all increased with normal load. These observations were more markedly displayed in the coarse-grained than in the fine-grained alumina. In the 0.7-μm fine-grained alumina, the wear process appeared to be mainly controlled by plastic deformation especially at low loads (e.g. < 10 N). At higher loads, however, both plastic deformation and grain boundary fracture processes seemed to be involved. In the 5-μm and 25-μm coarse-grained aluminas, the predominant material removal process was controlled by both intergranular and transgranular fractures.

Role of composition and microstructure in the abrasive wear of high-alumina ceramics

Analysis of Material Removal in Alumina Ceramic Honing

Wear performance of alumina-based ceramics - a review of the influence of microstructure on erosive wear

Grain size effect on abrasive wear mechanisms in alumina ceramics

Wear transitions and tribochemical reactions in ceramics

Impact-abrasive wear resistance of high alumina ceramics and ZTA

A Study of Parameters Affecting Wear Resistance of Alumina and Yttria Stabilized Zirconia Composite Coatings on Al-6061 Substrate

Study on the erosive wear behavior of Al2O3 ceramics

Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

Effect of Different Abrasive Particle Hardness on the Erosion Resistant Performance of Α-Al<sub>2</sub>o<sub>3</sub> Ceramics

Modelling the wear evolution of a single alumina abrasive grain: Analyzing the influence of crystalline structure

Effect of Different Abrasive Particle Hardness on the Erosion Resistant Performance of α-Al<sub>2</sub>O<sub>3</sub> Ceramics

Microstructure and Wear Behaviour of Ceramic Particles Strengthening Nial Based Composite

Erosion-Wear Property of α-Al2O3 Structure Ceramics with Different Experiment Parameters

Effect of different abrasive particle hardness on the erosion resistant performance of α-Al2O3 ceramics

Erosive Wear Performance and Mechanism of Engineering Ceramic Materials

Influence of the Reinforcement Phase Composition on the Structure and Abrasive Wear Resistance of Aluminum Matrix Composites Reinforced with B4C and SiC

The relation of mechanical properties and resistance erosion-wear of structure ceramic

A comparative study on tribological behavior of Al2O3, AlN, Si3N4 and ZrO2 ceramics sliding against polycrystalline diamond ball

A comparison of the erosive wear performance of particle reinforced aluminum matrix composites

Friction and wear performance of Al2O3 ceramics with elongated grains