Effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating
Jiuguo Deng,Wei Zhang,Xi Qiu,Quan Li,Qingsong Chen,Jian Yang,Yilong Zhong,Changda Zhu,Hao Liu,Sha Zhao,Qingyu Li,Mingyang Zhou,Ning Liu,Jijun Yang
DOI: https://doi.org/10.1016/j.jnucmat.2023.154592
IF: 3.555
2023-06-20
Journal of Nuclear Materials
Abstract:The effect of Au-ion irradiation on the morphology, microstructure and lead-bismuth eutectic (LBE) corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating was investigated. After irradiation, the surfaces of coatings were smoothened, and crystalline phase was formed in the coatings. After LBE corrosion at 650 °C, the irradiated samples presented a triple layer (interface Fe-Cr spinel, coating and surface Fe-oxide layer) consistent with the pristine sample, and the coating still maintained the low-consumption characteristic. Irradiation accelerated LBE corrosion, which could be attributed to the formation of grain boundary and defects that provided more diffusion channels for atoms.
materials science, multidisciplinary,nuclear science & technology