Abstract:In this work, two scanning speeds (2 mm/s and 8 mm/s) were employed to remelt the surface of an A356 cast Al alloy by a pulsed laser at 300 W, with microstructural features of the laser-remelted surface layers well characterized and correlated with their wear/corrosion resistance. Through high-quality microstructure characterizations, it is found that the as-received A356 alloy is comprised of coarse α-Al dendrites and interdendritic AlSi eutectics. After laser surface remelting (LSR) at both speeds, microstructure homogeneity is greatly improved due to the remarkable refinement of the dendrites and interdendrites. Hardness and wear tests show that surface hardness and wear rate of the 2 mm/s specimen are 71.6 ± 0.6 HV and 1.1 × 10 −3 mm 3 ·N −1 ·m −1 , while those of the 8 mm/s specimen are 67.2 ± 1.1 HV and 1.7 × 10 −3 mm 3 ·N −1 ·m −1 , respectively, markedly improved compared to the substrate (55.3 ± 0.5 HV and 2.8 × 10 −3 mm 3 ·N −1 ·m −1 ). Electrochemical test results reveal that self-corrosion potential (E corr ) and current (I corr ) of the 2 mm/s specimen are −0.82 V and 9.5 × 10 −7 μA, while those of the 8 mm/s specimen are −0.89 V and 1.8 × 10 −6 μA, respectively. After comparing with the substrate (−0.95 V and 4.3 × 10 −6 μA), the corrosion resistance of both the LSRed specimens is confirmed to be significantly enhanced. Comprehensive analyses reveal that after the LSR the simultaneously increased wear/corrosion resistance can be related to the largely homogenized microstructure, the enhanced supersaturation of Si in α-Al, and the refinement and redistribution of AlSi eutectics in the remelted layer.

Corrosion performance and microstructure of a Q370qENH weathering steel welded joint treated by the laser surface remelting method

Effect of Arc Surface Remelting on the Corrosion Resistance of 0cr19ni9 TIG Welding Joint

Surface Treatment of 0cr19ni9 Stainless Steel SMAW Joint by Plasma Melting

The Corrosion Resistance of 0cr19ni9 Stainless Steel Arc Welding Joints with and Without Arc Surface Melting

Correlating microstructural features with improved wear and corrosion resistance of laser surface remelted A356 alloy at different scanning speeds

Microstructure characteristics of Q345R-steel welded joints and their corrosion behavior in a hydrofluoric acid environment

Effects of Laser Welding on the Microstructure Evolution and Corrosion Resistance of a Novel Nitrogen-Containing Austenitic Stainless Steel QN2109

Comparative Analysis on Microstructure and Properties of Welding Joints of Q350EW and Q355GNH Weathering Structural Steel

Femtosecond Laser Treatment for Improving the Corrosion Resistance of Selective Laser Melted 17-4PH Stainless Steel

Influence of Ultraviolet Light and Alternating Wet-Dry Environments on the Corrosion Behavior of Weathering Steels

A comparative study of microstructure and corrosion resistance in DP980 steel joints under different laser welding method

Study on Microstructure and Properties of LZ50 Axle Steel Repaired by Laser Additive Remanufacturing

Weld morphology and mechanical properties in laser spot welding of quenching and partitioning 980 steel

Laser Shock Peening Improves the Corrosion Resistance of an E690 High-Strength Steel Cladding Layer

Revealing the microstructural evolution and its influence on mechanical properties of heterostructured steel fabricated by laser melting deposition

The role of copper in microstructures and mechanical properties of laser-welded Fe-19Ni-3Mo-1.5Ti maraging steel joint

Effects of Interlaminar Microstructural Inhomogeneity on Mechanical Properties and Corrosion Resistance of Multi-Layer Fiber Laser Welded High Strength Low Alloy Steel

Enhancing the corrosion properties and microhardness of titanium alloy by laser surface remelting

Microstructure and Corrosion Resistance of Underwater Laser Cladded Duplex Stainless Steel Coating after Underwater Laser Remelting Processing

Microstructure and Corrosion Properties of Laser-Welded SAF 2507 Super Duplex Stainless Steel Joints

High-Cycle Fatigue Performance of the Heat-Affected Zone of Q370qENH Weathering Bridge Steel