Hydrogen Interaction Characteristic of Nanoscale Oxide Films Grown on Iron–nickel Based Stainless Steel by Selective Thermal Oxidation
Cheng Zeng,Yakui Bai,Yunhan Ling,Zhiyuan Xin,Hao Liang,Xiukun Deng
DOI: https://doi.org/10.1016/j.ijhydene.2017.02.206
IF: 7.2
2017-01-01
International Journal of Hydrogen Energy
Abstract:Hydrogen isotopes, the reaction ingredients in the nuclear fusion plant, can easily permeate through the stainless steel (SS) substrate, leading to the so-called hydrogen degradation. Generally, a widely accepted way to reduce the hydrogen permeation is to prepare a barrier coating on the substrate. Nevertheless, the coated layer has the inherent problem of incompatibility with the heterogeneous base materials. In this work, in-situ selective oxidation was used to explore the optimal oxides with the improved hydrogen resistance. Two types of layers thermally formed at 450 degrees C and 750 degrees C, respectively, were selected to investigate their hydrogen interaction characteristics. Comprehensive analyses, including Raman spectra, XPS, EIS and AES, indicate that the oxide formed at 450 degrees C is a better candidate of hydrogen permeation barriers, probably due to the formation of protective layers of chromia and FeCr2O4, while the oxides obtained at 750 degrees C, though exhibiting a much more stable phase, can rarely reduce hydrogen diffusion through the shortcuts of defects. This finding provides a potential new way to prepare a hydrogen permeation barrier. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.