Abstract:Adding oxygen into the lead-cooled fast reactor (LFR) to generate a protective oxide layer is one of the most promising methods to mitigate the corrosion of structural materials caused by flowing lead-based coolants such as lead–bismuth eutectic (LBE). In LFRs, the growth-removal behavior of the protective oxide layer is influenced by various factors such as temperature, oxygen concentration, coolant velocity, and etc. Meanwhile, the formation of the oxide layer also changes the thermal–hydraulic characteristics and neutronics parameters of the reactor core. Historically, there has been a lack of research on the coupling effects of neutronics-thermal-hydraulics-materials (N-TH-M) under oxidation-corrosion conditions. In this paper, an N-TH-M multi-physics fields coupling framework was developed to study the key coupling parameters and oxidation corrosion characteristics of an LFR fuel assembly. The results indicate that the formation of the double oxide layer deteriorates the heat transfer between LBE/cladding, which results in the increases of 17.51 K and 10.04 K for maximum temperatures of fuel and cladding under the high oxygen concentration condition. The outer magnetite layer is severely dissolved by flowing LBE, while the inner Fe-Cr spinel layer exhibits good −dissolution resistance. The increase in oxygen concentration can inhibit the dissolution of magnetite and increase the thickness of magnetite, resulting in a 71 % reduction in the average removal thickness and a 5.88 μm increase in the average thickness of the magnetite layer. However, it has no significant effect on Fe-Cr spinel. The rise in coolant inlet temperature has a promoting effect on both the growth and the dissolution of the double oxide layer. With rise of coolant inlet temperature, the growth-promoting effect increases the average thickness of the double oxide layer from 14.11 μm to 27.82 μm. Additionally, the increase in coolant inlet velocity usually has a negative impact on the double oxide layer thickness.

Corrosion Kinetics and Mechanisms of 15-15Ti Steel in Flowing Liquid Lead-Bismuth Eutectic at 500°C

Corrosion kinetics of T91 steel under low oxygen conditions (10 −7 wt% O) in lead-bismuth eutectic at 500 °C

Corrosion Kinetics of T91 Steel under Low Oxygen Conditions (10-7 Wt% O) in Lead-Bismuth Eutectic at 500 ºc

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

High-Temperature Corrosion Behaviors of Structural Materials for Lead-Alloy-Cooled Fast Reactor Application

Long-Term Behaviors of Oxide Layer in Liquid Lead–Bismuth Eutectic (LBE), Part II: Model Applications

Insight into the fretting corrosion behavior of 316L steel in liquid lead-bismuth eutectic at 500°C

Corrosion Studies in Support of Medium-Power Lead-Alloy-Cooled Reactor

Study on the corrosion behavior of austenitic stainless 15-15Ti for nuclear fuel cladding in lead-bismuth eutectic alloy with oxygen control

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500$^\circ$C

Dissolution corrosion of FeCrAl alloy exposed to oxygen-depleted lead-bismuth eutectic containing Ni impurities at 600 °C

Corrosion behavior of magnetron sputtering Fe31Cr20Al17Ti16Nb16 high entropy coating in liquid lead-bismuth eutectic with different oxygen concentration at 500 °C

Corrosion behaviour of 11Cr1Si ferritic/martensitic steel in static liquid lead-bismuth eutectic at 450-550 °C

Study on the Corrosion Behavior of Aluminum Reinforced Austenitic Steel in Liquid Lead Bismuth at 550 °C

Corrosion Behavior and Surface Treatment of Cladding Materials Used in High-Temperature Lead-Bismuth Eutectic Alloy: A Review

Oxidation and dissolution behavior of FeCrNiAl based high entropy alloy and alumina-forming austenitic steel exposed to lead-bismuth eutectic (LBE)

A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead–bismuth eutectic flow pattern

Review of the studies on fundamental issues in LBE corrosion

Numerical investigation on the Multi-Physics coupling characteristics of Lead-Bismuth reactor fuel assembly based on oxidation corrosion behaviors

Study of lead-bismuth eutectic on material performance degradation and life assessment for modified 9Cr-1Mo steel under low cycle fatigue at high temperatures

Oxidation behavior of ferritic/martensitic steels in stagnant liquid LBE saturated by oxygen at 600°C