Abstract:Ferritic/martensitic (F/M) steel is considered as one of the most promising cladding materials for Lead-cooling fast reactors due to its favorable mechanical properties and radiation resistance. Quenching and partitioning (Q&P) process can further improve the mechanical properties of the F/M steels compared to conventional normalizing and tempering or quenching and tempering process. In this study, the Q&P process was employed to 9Cr F/M steels with different Si content (0, 0.4, 0.7, 1 wt.%), and the effect of Si content on their microstructure and mechanical properties was studied. The microstructure was characterized through SEM, EBSD, and TEM. The mechanical properties at room and elevated temperatures (500, 600, 700 °C) were tested. The results indicated that the addition of Si (0 to 1 wt.%) leads to a slight decrease in the ultimate tensile strength (UTS)/yield strength (YS) of the F/M steel at room temperature from 1328.3/986.5 MPa to 1300.7/950.7 MPa, respectively. Meanwhile, the fracture elongation (FE) maintains at about 16%. Additionally, as the Si content increases from 0 to 1 wt.%, the UTS and YS of the samples at elevated temperatures show a similar trend. However, the FE of the samples initially increases at 500 °C, noticeably decreases at 600 °C, and eventually rises at 700 °C. Only the FE at 600 °C was lower compared to that at room temperature. Furthermore, the UTS and YS of the samples decrease with increasing temperature. Although Si addition brings a higher solid solution strengthening effect, it is offset by the coarsening of block size and the formation of δ-ferrite. As a result, a little change in the strength of the steel is obtained.

Corrosion behaviour of 11Cr1Si ferritic/martensitic steel in static liquid lead-bismuth eutectic at 450-550 °C

Influence of Si addition on the corrosion behavior of 9Cr ferritic/martensitic steel in static liquid lead-bismuth eutectic

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Synergy of stress and corrosion in a 12Cr ferritic/martensitic steel exposed to static liquid lead-bismuth eutectic at 550°C

Effect of Silicon on Dynamic/Static Corrosion Resistance of T91 in Lead-Bismuth Eutectic at 550 °C

Dissolution corrosion of FeCrAl alloy exposed to oxygen-depleted lead-bismuth eutectic containing Ni impurities at 600 °C

Corrosion Kinetics and Mechanisms of 15-15Ti Steel in Flowing Liquid Lead-Bismuth Eutectic at 500°C

Oxidation behavior of ferritic/martensitic steels in stagnant liquid LBE saturated by oxygen at 600°C

Interfacial microstructure and corrosion behavior of ODS FeCrAl alloy in oxygen-saturated lead-bismuth eutectic at 450 °C

Influence of temperature on the microstructural evolution of SIMP and T91 steels in liquid lead-bismuth eutectic: Experiments and molecular dynamics simulations

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Microstructure response and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after Au-ion irradiation

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Microstructure evolution and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after proton irradiation

Performance of the new ferritic/martensitic steel SIMP against liquid lead‐bismuth eutectic corrosion: Comparison with T91 and 316L steels

Evaluation of Intergranular Corrosion Susceptibility of 11cr Ferritic Stainless Steel by Dl-Epr Method

In-situ proton irradiation/lead-bismuth eutectic corrosion synergistic effect on corrosion behaviour of 11Cr1W1Si ferritic/martensitic steel

Corrosion kinetics of T91 steel under low oxygen conditions (10 −7 wt% O) in lead-bismuth eutectic at 500 °C

Stress Corrosion Behavior of T91 Steel in Static Lead–bismuth Eutectic at 480 °C

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500$^\circ$C

Effect of Si Content on the Microstructure and Mechanical Properties of a 9Cr Ferritic/Martensitic Steel after a Quenching and Partitioning Process