Stress Corrosion Behavior of T91 Steel in Static Lead–bismuth Eutectic at 480 °C

Jing Liu,Zhizhong Jiang,Shujian Tian,Qunying Huang,Yuejing Liu

DOI: https://doi.org/10.1016/j.jnucmat.2015.09.032

IF: 3.555

2016-01-01

Journal of Nuclear Materials

Abstract:The corrosion behavior of stressed C-rings made of martensitic steel T91 was investigated through constant strain tests. The specimens with different initial hoop stresses (0 MPa, 150 MPa and 300 MPa) were exposed to static oxygen saturated lead-bismuth eutectic (LBE) at 480 degrees C for 500 h, 1000 h and 1500 h, respectively. The results showed that no crack was found on the outer surface of all the specimens after exposure; and the microscopic analysis showed that the specimens were covered with two oxide layers, which included a magnetite outer layer and a Fe-Cr spinet inner layer. The transformation of spinel into magnetite at the spinel/magnetite interface might be promoted by stress, which increased the difference between the thickness of the inner and outer layers. Moreover, the steel loss was estimated by the observed oxide layers; it increased rapidly when the stress was above 300 MPa, and was about 1.3 times of when the stress was absent. (c) 2015 Elsevier B.V. All rights reserved.