Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Fatigue Behaviour of a 9Cr1MoNbV Martensitic Steel in a Liquid Metal*

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Environmentally assisted cracking of T91 ferritic-martensitic steel in heavy liquid metals

Liquid lead-bismuth eutectic embrittlement effect on the tensile properties of T91 steel at 350C

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Stress Corrosion Behavior of T91 Steel in Static Lead–bismuth Eutectic at 480 °C

Comparative Study of High-Cycle Fatigue and Failure Mechanisms in Ultrahigh-Strength CrNiMoWMnV Low-Alloy Steels

Effect of long-term aging on the low cycle fatigue behavior and microstructure of a 10% Cr martensitic steel with low nitrogen and high boron contents at 650 °C

Near-threshold fatigue crack growth behavior of 10% Cr martensitic steel welded joint with 9% Cr weld metal in high temperature air

Low-Cycle Fatigue Properties of P92 Ferritic-Martensitic Steel at Elevated Temperature

Low cycle fatigue behavior of 316LN stainless steel hollow specimen in air and liquid lead-bismuth eutectic

Liquid metal embrittlement of 12Cr ferritic/martensitic steel thin-walled tubes exposed to liquid lead-bismuth eutectic

The fatigue properties, microstructural evolution and crack behaviors of low-carbon carbide-free bainitic steel during low-cycle fatigue

Effect of microstructure on the fatigue crack growth behavior of 9%Cr martensitic steel at different stress ratios under 630 °C

Liquid metal embrittlement and deformation induced martensite: The case of 316 L austenitic steel LME by liquid eutectic gallium-indium

Study of lead-bismuth eutectic on material performance degradation and life assessment for modified 9Cr-1Mo steel under low cycle fatigue at high temperatures

Liquid metal embrittlement susceptibility of an oxide-dispersion strengthened FeCrAl alloy in contact with liquid lead-bismuth eutectic at 350 °C

Low-temperature fatigue of 316L and 316LN austenitic stainless steels

A comparative study on liquid metal embrittlement susceptibility of three FeCrAl ferritic alloys in contact with liquid lead-bismuth eutectic at 350°C