Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low-Cycle Fatigue Properties of P92 Ferritic-Martensitic Steel at Elevated Temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of Fatigue Load on High-Temperature Tensile Properties of P92 Steel

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Simulation of Cyclic Deformation Behavior of Ferritic P92 Steel Based on Unified Viscoplastic Model

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior

Multiaxial fatigue behaviour and damage mechanisms of P92 steel under various strain amplitudes and strain ratios at high temperature

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Remaining creep properties and fracture behaviour of P92 steel welded joint under prior low cycle fatigue loading

Fatigue-Creep Interaction Of P92 Steel And Modified Constitutive Modelling For Simulation Of The Responses

High-Temperature Low-Cycle Fatigue Behavior of HS80H Ferritic–Martensitic Steel Under Dynamic Strain Aging

Influence of the strain rate on the fatigue behaviour of fully ferritic high chromium steel and P91 steel at high temperatures

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint