Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

High-Temperature Low-Cycle Fatigue Behavior of HS80H Ferritic–Martensitic Steel Under Dynamic Strain Aging

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Mechanism of Fatigue-Life Extension Due to Dynamic Strain Aging in Low-Carbon Steel at High Temperature

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Effect of Fatigue Load on High-Temperature Tensile Properties of P92 Steel

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Low-Cycle Fatigue Properties of P92 Ferritic-Martensitic Steel at Elevated Temperature

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Fatigue life modeling for a low alloy steel after long-term thermal aging

Multiaxial fatigue behaviour and damage mechanisms of P92 steel under various strain amplitudes and strain ratios at high temperature

A comparative study of low cycle fatigue behavior and microstructure of Cr-based steel at room and high temperatures

Influence of the strain rate on the fatigue behaviour of fully ferritic high chromium steel and P91 steel at high temperatures