Fabrication of Polyether–Ether–Ketone Foams with Superior Properties and Mitigated Weld Lines by Microcellular Injection Molding

Yu-Teng Feng,Lin Wang,Hao-Yang Mi,Laifa Gu,Binbin Dong,Chuntai Liu,Changyu Shen

DOI: https://doi.org/10.1002/adem.202100766

IF: 3.6

2021-09-14

Advanced Engineering Materials

Abstract:Polyether-ether-ketone (PEEK) as an engineering plastic with excellent mechanical properties requires strict processing conditions. Introducing microcells in PEEK parts is beneficial for reducing the material cost and improving their tenacity. Herein, foamed PEEK parts were fabricated using microcellular injection molding with supercritical nitrogen as the blowing agent. Using the optimum processing conditions obtained from orthogonal array experiments based on finite element simulation. The foamed PEEK parts achieved a 10 % average weight reduction and displayed a typical sandwich structure with an average cell size of 30 μm in the core region. The cell size was larger while the cell density and skin layer thickness were smaller in the region near the gate than the region far from the gate. The foamed PEEK parts had a slight drop in the tensile modulus and tensile strength but a significant improvement in the elongation-at-break when compared with the solid parts. Moreover, the foamed PEEK parts with weld lines exhibited less reduction in tensile properties than the solid counterparts, attributing to their tighter interfacial adhesion at the weld line, which was resulted from the cell expansion and the entanglements of the molecular chain ends. This study successfully produced foamed PEEK parts with high weight reduction and ductility, and provided insights into the weld line mitigation through microcellular injection molding.This article is protected by copyright. All rights reserved.

materials science, multidisciplinary