Abstract:Mg 3 Sb 2 -based n-type materials are consisted of earth-abundant elements and possess comparable thermoelectric properties with n-type Bi 2 Te 3 at low temperatures, which make them promising candidates for cooling and power generation applications in terms of cost and performance. Substitution of Sb atom with chalcogen elements (Te, Se S) is a conventional method for n-type doping, but doping cations such as rare-earth elements and transition metals is also widely studied for its unique advantages. In this study, La and Mn were selected for co-doping of Mg3SbBi, and the thermoelectric performances of the doped materials were investigated. Mg 3 La 0.005 Mn x SbBi (0  x  0.015) polycrystalline samples were made by sintering the fine powders of the mother alloy after arc melting, in which elemental Mn and LaSb compound were included for n-type dual doping. Considering the loss of Mg at elevated temperatures by vaporization, the molar ratio of Mg, Sb, and Bi in the mixture for arc melting was set to 4 : 1 : 1 with excess Mg. Analysis shows that all the samples are n-type, and the electrical conductivity of Mg 3 La 0.005 Mn 0.015 SbBi increased by 62% from the Mn-free Mg 3 La 0.005 SbBi at 298 K. In addition, the lattice thermal conductivity (  lat ) decreased with increasing Mn content in the measured temperature range of 298-623 K. The minimum value of  lat was about 0.60 W m -1 K -1 in Mg 3 La 0.005 Mn 0.015 SbBi at 523 K, which is about 19% smaller than that of the Mn-free sample. As a result of these enhancements in thermoelectric performance, the maximum figure of merit ( zT max ) of 1.12 was obtained in Mg 3 La 0.005 Mn 0.01 SbBi and Mg 3 La 0.005 Mn 0.015 SbBi at 573 K, and the zT at 298 K increased by 73% to 0.35 in Mg 3 La 0.005 Mn 0.015 SbBi compared to Mn-free Mg 3 La 0.005 SbBi, which is beneficial to room-temperature applications.

Promoted application potential of p-type Mg3Sb1.5Bi0.5 for the matched thermal expansion with its n-type counterpart

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

All‐Mg3Sb2‐Based Module for Thermoelectric Power Generation

Enhanced thermoelectric performance of P-type CaMg2Bi1.98 and optimized CaAl2Si2-type Zintl phase module with equal cross-section area

Maximizing the performance of n-type Mg3Bi2 based materials for room-temperature power generation and thermoelectric cooling

Enhanced Thermoelectric Performance of p‐Type Mg3Sb2 for Reliable and Low‐Cost all‐Mg3Sb2‐Based Thermoelectric Low‐Grade Heat Recovery

Enhancing the Thermoelectric Performance of n‐Type Mg3Sb2‐Based Materials via Ag Doping

High thermoelectric performance and anisotropy studies of n-type Mg3Bi2-based single crystal

Wide-temperature-range thermoelectric n-type Mg3(Sb,Bi)2 with high average and peak zT values

Optimization of Thermoelectric Property of n‐Type Mg3Sb2 Near Room Temperature via Mn&Se Co‐Doping

Electronic Orbital Alignment and Hierarchical Phonon Scattering Enabling High Thermoelectric Performance p-Type Mg 3 Sb 2 Zintl Compounds

Boosting room-temperature thermoelectric performance of Mg 3 Sb 1.5 Bi 0.5 material through breaking the contradiction between carrier concentration and carrier mobility

High-Performance Low-Cost n-Type Se-Doped Mg3Sb2-Based Zintl Compounds for Thermoelectric Application

High thermoelectric performance at room temperature of n-type Mg3Bi2-based materials by Se doping

High-Performance Mg<sub>3</sub>Sb<sub>2-<i>x</i></sub>Bi<i><sub>x</sub></i> Thermoelectrics: Progress and Perspective

High performance of Mg3Bi1.5Sb0.5 based materials for power generation: Revealing the counter-intuitive effect of tuning Bi content on the thermoelectric properties

Enhanced thermoelectric performance of n-type Mg3Bi2-based materials by Se doping and alloying engineering

Next-generation thermoelectric cooling modules based on high-performance Mg3(Bi,Sb)2 material

Thermoelectric performance of p-type (Bi,Sb)2Te3 incorporating amorphous Sb2S3 nanospheres

Effect of Composition Adjustment on the Thermoelectric Properties of Mg3Bi2-Based Thermoelectric Materials

Thermoelectric Properties of N-type Mg 3 La 0.005 Mn x SbBi Materials Doped with La and Mn