Abstract:The thermoelectric performance of the p‐type Mg3Sb2‐based compound is improved by fully optimizing its carrier concentration, mobility, and lattice thermal conductivity. As a result, a unicouple comprised of p‐type Mg1.594Yb0.2Na0.006Zn1.2Sb2 and n‐type Mg3.2SbBi0.99Te0.01 is successfully constructed, and exhibits high conversion efficiency, good stability, and low cost, showing its great potential for low‐grade heat recovery. Bi2Te3‐based devices have long dominated the commercial market for thermoelectric cooling applications, but their narrow operating temperature range and high cost have limited their possible applications for conversion of low‐grade heat into electric power. The recently developed n‐type Mg3Sb2‐based compounds exhibit excellent transport properties across a wide temperature range, have low material costs, and are nontoxic, so it would be possible to substitute the conventional Bi2Te3 module with a reliable and low‐cost all‐Mg3Sb2‐based thermoelectric device if a good p‐type Mg3Sb2 material can be obtained to match its n‐type counterpart. In this study, by comprehensively regulating the carrier concentration, carrier mobility, and lattice thermal conductivity, the thermoelectric performance of p‐type Mg3Sb2 is significantly improved through Na and Yb doping in Mg1.8Zn1.2Sb2. Moreover, p‐ and n‐type Mg3Sb2 are similar in terms of their coefficients of thermal expansion and their good performance stability, thus allowing the construction of a reliable all‐Mg3Sb2‐based unicouple. The decent conversion efficiency (≈5.5% at the hot‐side temperature of 573 K), good performance stability, and low cost of this unicouple effectively promote the practical application of Mg3Sb2‐based thermoelectric generators for low‐grade heat recovery.

Enhancing the Thermoelectric Performance of n‐Type Mg3Sb2‐Based Materials via Ag Doping

Thermoelectric performance improvement of p-type Mg3Sb2-based materials by Zn and Ag co-doping

Realizing Cd and Ag codoping in p-type Mg3Sb2 toward high thermoelectric performance

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Optimization of Thermoelectric Property of n‐Type Mg3Sb2 Near Room Temperature via Mn&Se Co‐Doping

Realizing High Thermoelectric Performance in N‐Type Mg3(Sb, Bi)2‐Based Materials via Synergetic Mo Addition and Sb–Bi Ratio Refining

Maximizing the performance of n-type Mg 3 Bi 2 based materials for room-temperature power generation and thermoelectric cooling

Synergistic Effect of Band and Nanostructure Engineering on the Boosted Thermoelectric Performance of n‐Type Mg3+δ(Sb, Bi)2 Zintls

Maximizing the performance of n-type Mg3Bi2 based materials for room-temperature power generation and thermoelectric cooling

Enhancing the Thermoelectric Performance of P-Type Mg3Sb2 Via Codoping of Li and Cd

Enhancing Thermoelectric Performance in P‐Type Sb 2 Te 3 ‐Based Compounds Through Nb─Ag Co‐Doping with Donor‐Like Effect

Enhancing the Thermoelectric Performance of Mgagsb-Based Materials with Heavy Zn-Doped

High Thermoelectric Performance at Room Temperature of N-Type Mg 3 Bi 2 -Based Materials by Se Doping

High‐Performance N‐type Mg3Sb2 Towards Thermoelectric Application Near Room Temperature

Enhanced Thermoelectric Performance of p‐Type Mg3Sb2 for Reliable and Low‐Cost all‐Mg3Sb2‐Based Thermoelectric Low‐Grade Heat Recovery

Promoted application potential of p-type Mg3Sb1.5Bi0.5 for the matched thermal expansion with its n-type counterpart

Enhanced thermoelectric performance of n-type Mg3Bi2-based materials by Se doping and alloying engineering

All‐Mg3Sb2‐Based Module for Thermoelectric Power Generation

Enhanced Thermoelectric Performance in P-Type Mg 3 Sb 2 Via Lithium Doping

High thermoelectric performance at room temperature of n-type Mg3Bi2-based materials by Se doping

Improving p-type thermoelectric performance of Mg2(Ge,Sn) compounds via solid solution and Ag doping