Abstract:This study reports the investigation of the morphology of the surface damaged during the laser scribing of glass and the analysis of the corresponding interaction mechanism between the laser and glass. In this study, the soda lime glass of 1.1 mm thick is scribed by an ultraviolet (UV) picosecond laser (Nd:YVO4) by varying laser power, scan speed and number of scans. From the analysis of experimental results, it is found that the surface morphology can be classified as three groups such as swelled surface, wave pattern (either shallow or deep) and groove depending on the accumulated laser energy per unit beam spot. The accumulation of the large laser energy (12–30 × 10−4 J) into the material induces volume meting and local vaporization below the surface without material removal, which makes bubbles inside glass volume and swelled surface through volume expansion. With the decrease of the energy accumulation (4.2–9 × 10−4 J), the surface morphology is changed into shallow wave pattern by slight material removal. With further decrease of the laser energy accumulation (1.4–3 × 10−4 J), either deep wave or groove morphology is obtained due to the increase of the material removal. Under very low laser energy accumulation region (0.3–1.05 × 10−4 J), the groove shape is only formed. In particular, the groove morphology without cracking is successfully produced within the range of 0.3–0.5 × 10−4 J. The threshold laser energy accumulation for surface damage is found to be around 0.25–0.3 × 10−4 J. Below this energy accumulation, modification in the surface morphology doesn’t occur. It is also found that the groove morphology is hard to obtain by even multiple laser scans if it is not well formed by single laser scan. The cracks produced during the scribing process can be characterized with several propagation morphologies. At the region of the relatively low laser energy accumulation, cracks propagating across the scan direction are only generated. However, cracks propagating both across and along the scan direction are found with the increase of the laser energy accumulation. Huge cracks (arc or sinusoidal curve shape) of several millimeters in size are produced under the very large laser energy accumulation.

Error analysis in 532 nm nanosecond laser cutting of solar glass

Analysis and comparison of laser cutting performance of solar float glass with different scanning modes

Investigation of solar float glass hole cutting using 532 nm nanosecond pulsed laser

Influence of helix geometric parameters on surface quality during laser cutting of photovoltaic float glass

532 nm Nanosecond laser cutting solar float glass: Surface quality evaluation with different laser spot positions in field lens

Dual Laser Beam Revising the Separation Path Technology of Laser Induced Thermal-Crack Propagation for Asymmetric Linear Cutting Glass

Cutting The Closed Curve Shape Inside Glass With Laser Induced Thermal-Crack Propagation

Yag Laser Cutting of Multi-Layer Soda-Lime Glasses

Investigation of the surface morphology in glass scribing with a UV picosecond laser

Dimethicone-aided laser cutting of solar rolled glass

Semiconductor laser asymmetry cutting glass with laser induced thermal-crack propagation

Analysis of the Effects on Ultra-Short Laser Pulse Beam Quality Caused by Errors in Optical Systems

High quality full ablation cutting and stealth dicing of silica glass using picosecond laser Bessel beam with burst mode

A novel monitoring method of nanosecond laser scribing float glass with acoustic emission

Thick Glass High-Quality Cutting by Ultrafast Laser Bessel Beam Perforation-Assisted Separation

Effect of Focus Position and Shear Stresses on the Crack Sectional Shape in Semiconductor Laser Linear Cutting Glass

Experimental Investigation on Cutting Characteristics in Nanometric Plunge-Cutting of BK7 and Fused Silica Glasses

Effect of thermal stresses on chip-free diode laser cutting of glass

Low-Temperature Gas Cooling Correction Trajectory Offset Technology of Laser-Induced Thermal Crack Propagation for Asymmetric Linear Cutting Glass

Laser cutting sandwich structure glass–silicon–glass wafer with laser induced thermal–crack propagation

Effect of microstructure on thermal field distribution of absorption glass with nanosecond laser-irradiated