Combustion Synthesis and Characterization of Ultra-High-Temperature NbB2–HfB2 Solid Solutions

V. V. Kurbatkina,E. I. Patsera,T. A. Sviridova,N. A. Kochetov,E. A. Levashov

DOI: https://doi.org/10.3103/s1061386223040143

2024-01-19

International Journal of Self-Propagating High-Temperature Synthesis

Abstract:This paper presents an in-depth study on the combustion synthesis, solid-solution formation, processing, and characterization of NbB 2 –HfB 2 ceramics, aiming to explore their potential applications, particularly in industries requiring high-performance materials. We conducted macrokinetic measurements and fitted regression models to predict combustion temperature and velocity for compositions ranging from 50 to 100% HfB 2 . A combined method of ball milling and hot pressing was developed for processing the combustion products into dense ceramics. These methods resulted in samples with relative densities reaching 97%, hardness of up to 34 GPa, and Young's modulus of up to 530 GPa, with NbB 2 –50% HfB 2 solid solution exhibiting the best mechanical properties. The study revealed a linear increase in thermal properties and density with the rise in HfB 2 content. The thermal conductivity of the solid solutions in the Nb–Hf–B system ranged from 34 to 40 W/mK and was found to increase with temperature, making these ceramics suitable for ultra-high-temperature applications. The findings have significant implications for aerospace and high-performance engineering sectors and provide a solid foundation for further investigation of Nb–Hf–B ceramics under real-world operational conditions.