Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

The Structure and Properties of the Promising Ultra-High-Temperature HfB2–HfC–SiC Ceramics Obtained from Heterophase SHS Powders

High temperature ablation of hot pressed HfC‐SiC ceramics

Phase evolution and oxidation resistance of Si3N4/HfB2/HfB C N1–– ceramic nanocomposites prepared from tailored preceramic polymers

HfB 2 -SiC ceramics fabricated by reactive melt infiltration and its long-term oxidation behavior at 1650°C

Insights into the Bond Behavior and Mechanical Properties of Hafnium Carbide under High Pressure and High Temperature

Structure and Oxidation Behavior of Multicomponent (Hf,Zr,Ti,Nb,Mo)C Carbide Ceramics

Effect of lanthanum on the structure, properties and high-temperature oxidation patterns of the (Hf,Ta)B 2 –SiC ceramics

Low temperature sintering of Hf0.95Nb0.05B2-based ceramics with submicron-scaled grains and enhanced mechanical properties

Densification, microstructure and properties of ultra-high temperature HfB2 ceramics by the spark plasma sintering without any additives

Polymer-derived SiHfN ceramics: From amorphous bulk ceramics with excellent mechanical properties to high temperature resistant ceramic nanocomposites

Effect of SiC on Microstructure, Phase Evolution, and Mechanical Properties of Spark-Plasma-Sintered High-Entropy Ceramic Composite

Combustion Synthesis and Characterization of Ultra-High-Temperature NbB2–HfB2 Solid Solutions

Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Exceptional hardness and thermal properties of SiC/(Hf,Ta)C(N)/ (B)C ceramic composites derived from single‐source precursor

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Pressureless densification of HfB2-based ceramics using HfB2 powders by borothermal reduction

Ablation behaviour of ultra-high temperature ceramic matrix composites: Role of MeSi2 addition

Preparation of silicon-nitride ceramic fibers with hafnium compounds loaded on the surface and the high temperature properties

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites