Abstract:To enhance the ablation resistance of graphite, double-glow plasma surface metallurgy technology was used to efficiently prepare Ta, TaC and Ta/TaC coatings on the graphite. All coatings exhibited a uniform and dense structure, with no microdefects at the interfaces, and the phases of the coatings closely matched the targets. The introduction of the Ta transition layer did not significantly improve the hardness or micro scratch performance of the Ta/TaC coating but greatly enhanced the toughness. Severe ablation occurred on the graphite substrate at 26.5 kW/cm 2 , while noticeable signs of ablation on the Ta and the two TaC coatings was at 61.9 kW/cm 2 and 70.7 kW/cm 2 , respectively. Although the Ta transition layer did not enhance the ultimate failure power of the Ta/TaC coating, notably, the TaC coating lost its protective function after 10 cycles, whereas the Ta/TaC coating remained protective for 15 cycles, exhibiting superior resistance to cyclic ablation. This can be attributed to the Ta transition layer, which not only prevented crack formation and spalling of the Ta/TaC coating but also maintained the integrity of the coating by flowing and filling the TaC coating. Additionally, the Ta oxides formed during the early cycles also provided a certain degree of protection during subsequent ablation tests. The findings of this study can provide an effective approach for the design and fabricating technology of graphite ablation-resistant coatings.

Residual stress and ablation behavior of CVD TaC coatings on graphite

Ablation behavior of Ta, TaC and Ta/TaC coatings on graphite under high-energy laser irradiation

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Tribological Properties of Ta‐C‐N and Ta‐N Thin Films

Research progress on tantalum carbide coatings oncarbon materials

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Tetrahedral Amorphous Carbon Coatings with Al Incorporation Deposited by a Hybrid Technique of Sputtering and Arc Evaporation

Effect of TaC Content on Microstructure and Properties of W-TaC Composites

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Microstructure, mechanical and tribological properties of graphite-like carbon coatings doped with tantalum

Effect of TiC addition on the microstructure and properties of Ni3Ta–TaC reinforced Ni-based wear-resistant coating

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Tribological and Corrosion Properties of the CoCrAlYTaSiC-xCNTs Coatings Deposited by Laser Cladding

The Effect of RF Sputtering Power on Structural, Nanomechanical and Tribological Properties of Single Layered TaN Coatings

FRICTION AND WEAR PERFORMANCE OF AN ELECTROSPARK-DEPOSITED Ta COATING ON CrNi3MoVA ST

Influence of Nitrogen Partial Pressure on Structure, Mechanical and Tribological Properties of TaCN Coatings

Behavior of Ti Coating in CBN/Ti/Vitrified Bond Gradient Materials

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings

Ablation behavior of high-entropy carbides ceramics (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C upon exposition to an oxyacetylene torch at 2000 °C