Abstract:To further the anti-ablation property of carbon/carbon composites (C/Cs) at extreme-high temperature, Cr-ZrC coating is fabricated on SiC-coated C/Cs. The anti-ablation properties of the ZrC coatings modified by various content of Cr are tested by oxyacetylene flame (heat flux: 2.4 MW/m(2)). Compared with pure ZrC coating, the ablation resistance property of the sprayed Cr-ZrC coating indicates an effective improvement. Cr acts as an accelerant by facilitating the liquid ZrO2 sintering and form a close structure. This dense structure can alleviate oxygen penetration. As the content of Cr increase (10 wt%, 15 wt% and 20 wt%), after cooling can also detect the retaining of tetragonal-ZrO2 (t-ZrO2). The phase transformation from t-ZrO2 to monoclinic ZrO2 (m-ZrO2) can lead to the volume expansion. The retaining of t-ZrO2 shows the phase transformation is impeded, which contributes to the thermal stability of the Cr modified ZrC coating. In the specimen, oxygen mainly diffuse through micropores, microcracks and grain boundaries. For Cr-ZrC coating, these diffuse ways could be partly or completely sealed by melted Zr-O-Cr coating during ablation test, which can effectively protect C/Cs during the oxyacetylene ablation test. When the content of Cr is 15 wt%, on the surface can form dense dendritic structure, which can effectively protect C/Cs from ablation.

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings

Microstructure and Ablation Properties of SiC/ZrB2–SiC/ZrB2/SiC Multilayer Coating on Graphite

Ablation resistance of ZrB2SiC/SiC coating prepared by pack cementation for graphite

Microstructure and Properties of ZrC-SiC Multi-Phase Coatings Prepared by Thermal Evaporation Deposition and an In-Situ Reaction Method

Study on the Ablation Resistance of ZrB2-SiC-LaSi2 Coating Prepared on the C/C Composites

Effect of the Surface Microstructure of Sic Inner Coating on the Bonding Strength and Ablation Resistance of Zrb2-Sic Coating for C/C Composites

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Ablation Mechanism and Properties of ZrB2-ZrC-SiC Coating with Micro-Submicron Reinforced Structure

Microstructure Characteristics and Ablation Behavior of an Al1.92 Cr0.08 O3-SiC-ZrC Anti-Ablation Coating

Microstructure and Ablation Mechanism of SiC-ZrC-Al2O3 Coating for SiC Coated C/C Composites under Oxyacetylene Torch Test

Study on Ablation Behavior of ZrB2-SiC Coating Based on the High Thermal Conductivity Substrate

Effect of CVD ZrB2 Coating Thickness on Anti-Ablation Performance of C/SiC Composites

Surface Optimization of ZrC–SiC Inner Layer to Enhance Ablation Property of SiC/ZrC–SiC Multi-Layer Coating for C/C Composites

Ablation behavior and mechanism of SiCnw modified SiC-ZrC coating for graphite under a plasma ablation flame

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Microstructures and Ablative Properties of ZrC Coating by Chemical Vapor Deposition

Investigation on Ablation Characteristics of C/C Composites with ZrC/SiC Coating

Effect of silicon/graphite ratio and temperature on oxidation protective properties of SiC/ZrB2–SiC coatings prepared by pack cementation

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration