Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying
Zhe Zhou,Furong Niu,Xiangfen Hu,Xianfeng Yang,Peng Liu,Long Zhang,Xizhi Fan,Weiguo Mao,Bei Zhang,Zexu Sun,Maozhong Yi
DOI: https://doi.org/10.1002/adem.202001457
IF: 3.6
2021-03-17
Advanced Engineering Materials
Abstract:<p>A W/ZrC/SiC multilayer coating was prepared on C/C composites by reactive melt infiltration (RMI) and atmospheric plasma spray (APS). The morphology and microstructure of the coating were characterized by scanning electron microscopy coupled with energy dispersive spectrometry (SEM‐EDS), X‐ray diffraction (XRD), focused ions beam (FIB) and transmission electron microscope (TEM). Microstructure analysis revealed that the gradient coatings exhibit smooth surface morphology, well‐defined interfaces, uniform thickness and highly dense architecture. After 60 s of ablation, the linear ablation rates (LAR) and mass ablation rates (MAR) of the coated composites stand at 2.58×10<sup>−3</sup> mm/s and 5.25×10<sup>−3</sup> g/s, respectively. In general, the reason for the great ablation resistance of W/ZrC/SiC coated C/C composites was the comprehensive effect of multilayer coating. The outer W coating was used as the first barrier layer to resist most thermal shocks. Then the molten eutectics SiO<sub>2</sub>‐ZrO<sub>2</sub> formed in ZrC/SiC layer at service temperature could fill the pores and acted as a second diffusion barrier for oxygen and heat.</p><p>This article is protected by copyright. All rights reserved.</p>
materials science, multidisciplinary