Abstract:Objectives: (1) To synthesize 3mol% yttria-stabilized zirconia (3Y-TZP) powders via coprecipitation route, (2) to obtain zirconia ceramic specimens, analyze surface characteristics, and mechanical properties, and (3) to compare the processed material with three reinforced dental ceramics. Methods: A coprecipitation route was used to synthesize a 3mol% yttria-stabilized zirconia ceramic processed by uniaxial compaction and pressureless sintering. Commercially available alumina or alumina/zirconia ceramics, namely Procera AllCeram (PA), In-Ceram Zirconia Block (CAZ) and In-Ceram Zirconia (IZ) were chosen for comparison. All specimens (6mmx5mmx5mm) were polished and ultrasonically cleaned. Qualitative phase analysis was performed by XRD and apparent densities were measured on the basis of Archimedes principle. Ceramics were also characterized using SEM, TEM and EDS. The hardness measurements were made employing Vickers hardness test. Fracture toughness (K(IC)) was calculated. Data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (alpha=0.05). Results: ANOVA revealed that the Vickers hardness (p<0.0001) and fracture toughness (p<0.0001) were affected by the ceramic materials composition. It was confirmed that the PA ceramic was constituted of a rhombohedral alumina matrix, so-called alpha-alumina. Both CAZ and IZ ceramics presented tetragonal zirconia and alpha-alumina mixture of phases. The SEM/EDS analysis confirmed the presence of aluminum in PA ceramic. In the IZ and CAZ ceramics aluminum, zirconium and cerium in grains involved by a second phase containing aluminum, silicon and lanthanum were identified. PA showed significantly higher mean Vickers hardness values (H(V)) (18.4+/-0.5GPa) compared to vitreous CAZ (10.3+/-0.2GPa) and IZ (10.6+/-0.4GPa) ceramics. Experimental Y-TZP showed significantly lower results than that of the other monophased ceramic (PA) (p<0.05) but it showed significantly higher fracture toughness (6.0+/-0.2MPam(1/2)) values when compared to the other tested ceramics (p<0.05). Significance: The coprecipitation method used to synthesize zirconia powders and the adopted ceramic processing conditions led to ceramics with mechanical properties comparable to commercially available reinforced ceramic materials.

Preparation and thermal insulation properties of TPMS 3Y-TZP ceramics using DLP 3D printing technology

Improved Mechanical Properties of 3YSZ Ceramics Prepared by Pressure-less Sintering Assisted by Cold Sintering under Mild Conditions

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

3D printing of TPMS structural ZnO ceramics with good mechanical properties

Effective thermal conductivity and heat transfer characteristics of a series of ceramic TPMS lattice structure

Influence of sintering temperature on the thermal conductivity of digital light processing 3D-printed yttria-stabilized zirconia ceramic

Preparation and stereolithography 3D printing of ultralight and ultrastrong ZrOC porous ceramics

Preparation of excellent performance ZTA ceramics and complex shaped components using digital light processing 3D printing technology

Fabrication and mechanical properties of triply period minimal surface porous alumina ceramics based on Digital Light Processing 3D printing technology

Digital Light Processing 3D‐Printed Porous Yttria‐Stabilized Zirconia with High‐Thermal Shock Resistance

Mechanical and electrical properties of 3Y‐TZP/TiSi2 composites sintered at different temperatures

3D printing of lead zirconate titanate piezoelectric ceramics via digital light processing (DLP)

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Fabrication of fine and complex lattice structure Al2O3 ceramic by digital light processing 3D printing technology

Advancements in DLP 3D Printing: High Strength Alumina Toughened Zirconia Ceramics for Biomedical Applications

Investigation of mechanical properties and low-temperature degradation of dental 3Y-TZP ceramics fabricated by stereolithography in combination with microwave sintering

3D printing of hollow lattice structures of ZrO2(3Y)/Al2O3 ceramics by vat photopolymerization: Process optimization, microstructure evolution and mechanical properties

Three-Dimensional Printing of Yttrium Oxide Transparent Ceramics via Direct Ink Writing

The study of mechanical properties of Ti3SiC2/Y TZP ceramics composites

Y-TZP ceramic processing from coprecipitated powders: a comparative study with three commercial dental ceramics

Evaluation of Zirconia Ceramic Processed by Digital Light 3D Printing Applicated as Solid-Electrolyte Sensor