Investigation of mechanical properties and low-temperature degradation of dental 3Y-TZP ceramics fabricated by stereolithography in combination with microwave sintering

Li Wang,Yang Jiao,Lian Yao,Yang Sheng,Zongdong Hao,Weizhe Tang,Rui Dou

DOI: https://doi.org/10.1016/j.jmbbm.2023.106211

Abstract:The purpose of this study was to obtain dental ceramic materials with excellent mechanical properties and high resistance to low temperature degradation (LTD) via stereolithography (SLA) in combination with microwave sintering (MWS). The results have shown that the unaged MWS-1425 °C 3Y-TZP ceramics with uniform microstructure have high density up to 99.04% and excellent mechanical properties (Vickers hardness 14.07 GPa, fracture toughness 4.32 MPa m1/2, flexural strength 947.87 MPa). After 50 h of LTD, the m-phase content of MWS 3Y-TZP ceramics accounts for only 10.3%. In addition, the surface roughness increases by only 1.3 nm, the degraded depth is less than 5 μm, and the flexural strength exceeds 900 MPa. This exhibits the high resistance to LTD and excellent mechanical properties of dental 3Y-TZP ceramics can be obtained.