Preparation and characterization of new sealing glasses based on Li2O-NiO-P2O5 system

Hany Abo-Mosallam,Ebrahim A. Mahdy

DOI: https://doi.org/10.1007/s11771-022-5033-6

2022-05-01

Journal of Central South University

Abstract:A series of glass are synthesized via a melt quenching technique based on the Li2O-NiO-P2O5 system. The concentration of nickel oxide varies from 5% to 15% in molar fraction. XRD pattern verifies the amorphous nature of prepared glass samples with 5%, and 10% nickel oxide in molar fraction. While Li3P and Ni2P4O12 phases are precipitated with a high nickel content up to 15% in molar fraction. As nickel is substituted for lithium, a systematic increase in glass transition temperature (Tg) and glass softening temperatures (Ts) is observed. This is greatly related to the increased structure, coherence in the glass network. Structural investigation showed that Ni2+ spectra are present in both octahedral and tetrahedral sites. Physical properties such as glass density ((2.38±0.1)−(2.46±0.1) g/cm3), and molar volume ((42.28±0.1)−(39.15±0.1) cm3/mol) are examined. The NiO/Li2O replacements led to a decrease in the dissolution rate of the resultant amorphous materials from 1.53×10−5 to 3.20×10−6 g/(cm2·min). Thermal expansion coefficients CTE of the glasses are diverse from 157×10−7to 96×10−7 °C−1 over the temperature range of 25 −250 °C. The prepared glasses are expected to be useful as a low-temperature sealing material.

metallurgy & metallurgical engineering