Influence NiO on the structure, elastic properties and buildup factor of BaO-CdO-borosilicate glasses

M. I. Sayyed,M. Abdo,H. Elhosiny Ali,H. A. Ahmed,M. S. Sadeq

DOI: https://doi.org/10.1088/1402-4896/acdc5d

2023-06-08

Physica Scripta

Abstract:In this work, the structure, elasticity parameters, and buildup factor of borosilicate glasses doped with BaO, CdO and NiO have been studied. Infrared (IR) spectroscopy was utilized to study the internal structure of the present system. IR spectra are broad, especially since the superposition between the borate and silicate occurs in the same spectral region. A deconvolution process was carried out to extract these spectra into their individual bands. The N4 values were found to barely increase from 37.9 % for 1 mol% of NiO reaching 39.5 % for 4 mol% of NiO. A such increase indicates the transformation of BO3 to BO4 units with further additions of NiO. The N4 values were used along with the dissociation energies density and packing density parameters to calculate the elastic moduli; Young, shear, bulk, and Poisson ratio. The obtained values of Young's modulus increase with further NiO additions. This increased behavior of Young's modulus demonstrates the augmented ability of the current glasses to withstand variations in their length under lengthwise tensile tension or compression with further NiO additions. The rest of the elasticity moduli showed increased behaviors as well. These increased behaviors support the results obtained from structural properties analyses. An increment of BO4 units with decreasing the nonbridging oxygens (NBO) in the internal structure of present glasses produces an increase in the elastic parameters of these glasses. At photons energy of 0.2 MeV, the values of energy exposure buildup factor (EBF) are low for glasses that have a high concentration of CdO (low concentration of NiO), but the value of EBF is larger for glasses that have a low concentration of CdO (high concentration of NiO).

physics, multidisciplinary