Abstract:This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact for c‐Si solar cells. The stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm2. Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. Carrier selective contacts with passivation effects are considered to have a significant influence on the performance of crystalline silicon (c‐Si) solar cells. It is essential for electron selective contact materials to meet the requirements of ultra‐low contact resistance and excellent passivation effects. This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact. It is found that the stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm (14.6 mΩ cm2 for the n‐Si/a‐Si:H/Li3PO4/TiO2/Al contact). Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. The characterization of the n‐Si/Li3PO4/TiO2 interface reveals that phosphorus diffusion into silicon plays a crucial role in achieving the ultra‐low contact resistivity, while the presence of PO43− groups helps in fixing hydrogen atoms to maintain the desired chemical passivation effect. Finally, a silicon heterojunction solar cell (SHJ) with a rear full‐area configuration of a‐Si:H/Li3PO4/TiO2/Al is successfully demonstrated achieving an impressive power conversion efficiency of 22.89%. The result proves the efficacy of employing hydrogen‐rich low‐work function metal oxide stacks as electron selective passivating contacts.

Efficient silicon solar cells with highly conductive zirconium nitride electron-selective contacts

Annealing-free, electron-selective ohmic contacts using zirconium oxide and aluminum for n-type crystalline silicon solar cells

Influence of contact characteristics of SnO2/P on fill factor of solar cell

Enhancing poly-Si contact through a highly conductive and ultra-thin TiN layer for high-efficiency passivating contact silicon solar cells

Self‐Diffusion Effect Assisted TiO2/Li3PO4 Electron Selective Passivating Contact in Silicon Solar Cells Approaching 23% Efficiency

The 18.3% Silicon Solar Cells with Nano-Structured Surface and Rear Emitter

Interfacial engineering of ZnS passivating contacts for crystalline silicon solar cells achieving 20% efficiency

A High-Quality Dopant-Free Electron-Selective Passivating Contact Made from Ultra-Low Concentration Water Solution

Sn‐doped Nb2O5 films as effective hole‐selective passivating contacts for crystalline silicon solar cells

Design and Optimization of SiOx/AZO Transparent Passivating Contacts for High‐Efficiency Crystalline Silicon Solar Cells

Tunable work function of molybdenum oxynitride for electron-selective contact in crystalline silicon solar cells

Chromium Trioxide Hole-Selective Heterocontacts for Silicon Solar Cells

Electron‐Selective Strontium Oxide Contact for Crystalline Silicon Solar Cells with High Fill Factor

Passivating Contact with Phosphorus‐Doped Polycrystalline Silicon‐Nitride with an Excellent Implied Open‐Circuit Voltage of 745 mV and Its Application in 23.88% Efficiency TOPCon Solar Cells

Regionalizing Nitrogen Doping of Polysilicon Films Enabling High‐Efficiency Tunnel Oxide Passivating Contact Silicon Solar Cells

Conductive Hole-Selective Passivating Contacts for Crystalline Silicon Solar Cells

Efficient Silicon Solar Cells with Aluminum‐Doped Zinc Oxide‐Based Passivating Contact

Numerical and experimental exploration towards a 26% efficiency rear-junction n-type silicon solar cell with front local-area and rear full-area polysilicon passivated contacts

Enhancing Adhesion and Reducing Ohmic Contact through Nickel–Silicon Alloy Seed Layer in Electroplating Ni/Cu/Ag

A silicon oxide-based highly transparent passivating contact for crystalline silicon solar cells approaching efficiencies of 23%

Modulation of the TCO/MoO x Front Contact Enables >21% High-Efficiency Dopant-Free Silicon Solar Cells