Abstract:The investigation of damage development is essential for the design and optimization of hybrid structures. This paper provides a reference for the structural design of brittle–ductile hybrid LVI-resistant laminates through analyzing the damage development mechanism of carbon/Kevlar fabric-reinforced composite laminates. The effects of Kevlar fabric hybrid ply and intercalation on the damage development of carbon/Kevlar composite laminates under low-velocity impact (LVI) were investigated using quasi-static indentation (QSI). It was found that an increase in the Kevlar hybrid ratio significantly reduced the peak load and stiffness of these laminates (the maximum decreases in strength and stiffness were 46.03% and 41.43%, respectively), while laminates with identical hybrid ratios but different plying configurations maintained a comparable stiffness under QSI, with differences of less than 5%. Interestingly, Kevlar fibers exhibited irregular fractures as the yarn was splitting, while carbon fibers presented neat breaks, which indicated material-specific failure modes. Notably, the introduction of Kevlar hybridization beyond pure Kevlar configurations (KKKK) resulted in a decrease in the percentage of fiber damage (CCCC, CCCK, CCKK, and KCCK accounted for 80%, 79.8%, 70%, and 60% of fiber damage, respectively), attributed to an increase in resin cracks and lower levels of Kevlar yarn breakage. The internal damage diameter of specimens was accurately predicted from the diameter of visible damage on the QSI surface. Compared with CCCC and CCKK setups, which are affected by resin cracks formed via the carbon surface on the loading side propagating along the yarn direction (including the yarn settling direction), KCCK demonstrated less delamination between the first and second ply.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the influence of Kevlar cloth hybrid layers and insertion sequences on the mechanical properties and damage resistance of carbon fiber / Kevlar composite laminates by analyzing the damage development mechanism of carbon fiber / Kevlar cloth - reinforced composite laminates under quasi - static indentation (QSI). Specifically, the research aims to: 1. **Evaluate the influence of different Kevlar cloth mixing ratios and arrangement sequences on the mechanical properties (such as stiffness and strength) of composite laminates**: - The research found that as the mixing ratio of Kevlar cloth increases, the peak load and stiffness of the composite laminates decrease significantly, with the maximum decreases being 46.03% and 41.43% respectively. - Laminates with the same mixing ratio but different arrangement sequences maintain similar stiffness under QSI, with a difference of less than 5%. 2. **Analyze the failure modes of different materials**: - Carbon fibers show neat fractures when stressed, while Kevlar fibers show irregular fractures, indicating material - specific failure modes. 3. **Explore the influence of Kevlar cloth hybrid layers on the development of internal damage**: - After introducing the Kevlar hybrid layer, the proportion of fiber damage decreases, the resin cracks increase, and the Kevlar yarn breakage decreases. - Through QSI tests, the initiation and propagation processes of damage can be observed more accurately, thus providing a reference for structural optimization design. 4. **Establish the relationship between the internal damage diameter and the surface - visible damage diameter**: - The research found that the internal damage diameter can be accurately predicted through the surface - visible damage diameter, which is of great significance for understanding the damage mechanism of composite materials. In summary, through experiments and analysis, this paper aims to provide a reference for the structural design of brittle - ductile hybrid LVI - resistant laminates, especially by studying the damage development mechanism of carbon fiber / Kevlar composites under low - speed impact.

Effects of Carbon/Kevlar Hybrid Ply and Intercalation Sequence on Mechanical Properties and Damage Resistance of Composite Laminates under Quasi-Static Indentation

Enhanced damage tolerance and fracture toughness of lightweight carbon-Kevlar fiber hybrid laminate

Low-velocity Impact Damage Research on CFRPs with Kevlar-fiber Toughening

Delamination Propagation Manipulation of Composite Laminates under Low-Velocity Impact and Residual Compressive Strength Evaluation

Hybridization effect of Kevlar and glass fiber on carbon/epoxy composites to enhance the damage strength under low velocity impact. Part II: Numerical simulations

Investigation of Damage to Thick Composite Laminates under Low-Velocity Impact and Frequency-Sweep Vibration Loading Conditions

Changes in Dynamic Mechanical Behavior of Carbon Fiber Reinforced Polymer Laminates under Multiple Low Energy Impacts

Experimental Investigation of Low-Velocity Impact Behavior and CAI on Composite Laminates by Discrete Interleaved Toughening

Effect of Continuous Fiber Orientations on Quasi‐static Indentation Properties in 3D Printed Hybrid Continuous Carbon/kevlar Fiber Reinforced Composites

Cellulose Nanocrystal-Polyetherimide Hybrid Nanofibrous Interleaves for Enhanced Interlaminar Fracture Toughness of Carbon Fibre/epoxy Composites

Layer-wise damage prediction in carbon/Kevlar/S-glass/E-glass fibre reinforced epoxy hybrid composites under low-velocity impact loading using advanced 3D computed tomography

Low‐velocity impact damage and compression after impact behavior of CF/PEEK thermoplastic composite laminates

Damage and Failure Analysis of Hybrid Laminates with Different Ply-Stacking Sequences under Low-Velocity Impact and Post-Impact Compression

Study on impact properties of carbon/kevlar fiber hybrid composites

Numerical Study of the Damage Behavior of Carbon Fiber/Glass Fiber Hybrid Composite Laminates under Low-velocity Impact

Low-velocity impact and compression-after-impact behaviors of twill woven carbon fiber/glass fiber hybrid composite laminates with flame retardant epoxy resin

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Permanent Indentation and Damage Creation of Laminates with Different Composite Systems: an Experimental Investigation

Research on Interlayer Toughening and Damage Detection of Laser-Induced Graphene and Short Kevlar Fibers Aramid Fiber/Epoxy Resin Composites

Low-velocity Impact Analysis and Multi-Objective Optimization of Hybrid Carbon/basalt Fibre Reinforced Composite Laminate

Thickness effect on ballistic impact behavior of hybrid carbon/Kevlar composites