Low-Velocity Impact and Post-Impact Residual Flexural Properties of Kevlar/EP Three-Dimensional Angle-Interlock Composites

Juanjuan Shi,Yanwen Guo,Xiaomei Huang,Hongxia Chen,Haijian Cao

DOI: https://doi.org/10.3390/ma17030681

IF: 3.4

2024-02-01

Materials

Abstract:In this study, five three-dimensional angle-interlock fabrics with different warp and weft densities were fabricated using 1000D Kevlar filaments. The Kevlar/EP composites were prepared by vacuum-assisted molding techniques. The low-velocity impact property of the composite was tested, focusing on the effects of the warp and weft densities, impact energy, impactor shape, and impactor diameter. The damage area, dent depth, and crack lengths in the warp and weft direction were used to evaluate the impact performance, and the specimens were compared with plain-weave composites with similar areal densities. The dominant failure mode of the conical impactor was fiber fracture, while the dominant failure mode of the hemispherical impactor was fiber–resin debonding. The cylindrical impactor showed only minor resin fragmentation. The residual flexural strength of the composite after impact was tested to provide insights into its mechanical properties. The study findings will provide a theoretical basis for the optimization of the design of impact-resistant structures using such materials and facilitate their engineering applications.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the performance of three-dimensional angle-interlock (3DAI) composites under low-velocity impact and their residual bending performance after impact. Specifically, the paper mainly explores the following points:

1. **Influencing Factors**: The study investigates the effects of factors such as warp and weft density, impact energy, impactor shape, and diameter on the low-velocity impact performance of 3DAI composites.
2. **Damage Mechanisms**: The analysis covers damage modes under different impact conditions, including fiber breakage, matrix cracking, and fiber-matrix debonding.
3. **Residual Bending Performance**: The residual bending strength and modulus of the composites after impact are evaluated through three-point bending tests, along with changes in bending failure modes.

Through these studies, the paper aims to provide a theoretical foundation for optimizing the design of impact-resistant structural materials and to promote their engineering applications.