Abstract:Preparation of the low‐velocity and tension‐after‐impact testing specimens and damage mechanism observed on the z‐pin reinforced curved composites. This paper studies the influence of z‐pins on the impact resistance and residual tensile properties of composite large curvature components through low‐velocity impact and tension‐after‐impact tests to explore the damage mechanism. Unpinned and z‐pinned specimens with different diameters (0.3 and 0.5 mm) and spacing (3, 4, and 5 mm) were impacted at energies of 28 J and 14 J + 14 J and were stretched until failure. The theoretical models were used to predict impact dent depth and tensile strength, and the effectiveness of z‐pins and damage patterns were characterized by force‐time/displacement curves and through visual observation. The agreement between the experiments and predictions can thus validate the presented approach. Through the low‐velocity impact test, it is found that z‐pins with higher density and smaller diameter make the impact dent shallower and the surface damage less, thus showing better performance. Later, the impacted specimens mainly show delamination, explosion, breakage, and splitting after tension. During the first stage of the force‐displacement curves, since z‐pins mitigate the delamination, tensile strength shows a 29.58%–59.17% increase while in the third stage, a decrease of 3.95%–15.12% occurs due to initial damage caused by z‐pins. Highlights Different impact energies are implemented on large curved CFRP laminates of z‐pins with different diameters and spacing to explore the damage mechanism. Low‐velocity impact and tension‐after‐impact (TAI) tests are used to simulate the centrifugal force of the blade subjected to impact and rotation after impact. Z‐pinned group with a small diameter and high density causes less damage and tensile strength in the first stage increases while decreasing in the third stage compared with the unpinned group.

Experimental Investigation of Z-pin Insertion Angles on the Mechanical Behavior and Failure Mechanism of Compression after Impact for CFRP Laminates

Effect of Z-pin Insertion Angles on Low-Velocity Impact Mechanical Response and Damage Mechanism of CFRP Laminates with Different Layups

Effect of Ø 0.11 Mm Z-pinning on the Properties of Composite Laminates Via an Ultrasound Guided Insertion Process

Strengthening of Composite T-joints Using Ø 0.11 Mm Z-pins Via an Ultrasound-Guided Insertion Process

Minimizing the In-Plane Damage of Z-pinned Composite Laminates Via a Pre-Hole Pin Insertion Process

Micro-damage Initiation Evaluation of Z-Pinned Laminates Based on a New Three-Dimension RVE Model

Effect of Z-pin inclined angle on the impact damage suppression effectiveness for cross-ply composite laminates

Out-of-plane Properties and Failure Mechanism of Composite Laminates Reinforced with Carbon Z-pins

Experimental investigation on the double-position low velocity impact responses for Z-pinned composite laminates

Experimental investigation on the fracture toughness of Z-pins reinforced composite laminates

Experimental and Numerical Investigations on the Mode I Delamination Growth Behavior of Reinforced Laminates Via a ZPI (Z-Pin Pre-Hole Insertion) Technique

Experimental Investigation on the Double-Position Impact Responses and Damage Mechanism for Z-pinned Composite Laminates

Experimental Study on the Low-Velocity Impact and Post-Impact Flexural Properties of Curved CFRP Laminates Reinforced by Pre-Hole Z-pinning (PHZ) Technique

Experimental investigations into damage mechanism in the low‐velocity impact and tension‐after‐impact testing of z‐pin reinforced curved CFRP composite

Experimental Investigation of the Double Impact Position Effect on the Mechanical Behavior of Low-Velocity Impact in CFRP Laminates

Experimental and Numerical Study on the Mode I Delamination Toughness of Z-Pinned Composite Laminates

Experimental Investigation into Influences of Z-pin and Deltoid on Structural Properties and Damage Tolerance of CFRP T-joints

Experimental Investigation of Low-Velocity Impact Behavior and CAI on Composite Laminates by Discrete Interleaved Toughening

Comparison of Laminate Thickness on the Low Velocity Impact Behaviors for Z-pinned Composite Laminates

Low‐velocity impact resistance of the Z‐pin reinforced carbon fiber composite laminates

Low-velocity impact behavior and residual tensile strength of CFRP laminates