Abstract:This paper is a continuation study of the residual compressive strength of composite laminates after impact under hygrothermal conditions. Two carbon fibre/epoxy plywood specimens with different lay-ups ([45/-45/0/0/45/0/0/0/90/-45/0]s and [45/-45/0/90/0 /0/0/0/90/0/-45/45]s) were investigated, The materials were subjected to 500 h, 1000 h and 2000 h of service time in a climatic chamber at a temperature of 60 °C and 100% relative humidity, followed by low-velocity post-impact compression using an energy level of 15 J. Experimental and numerical simulations are used to study the residual compressive strength and damage extension of the material. Using the ultrasonic C-scan technique, the internal damage of the specimens was scanned, and the damage evolution in impact and compression tests was analysed. Damage evolution in impact and compression tests was investigated using ultrasonic C-scanning to scan the internal damage of the specimens. The strain change maps of the specimens during compression are studied using the Digital Imaging (DIC) technique. Vumat subroutine coded in Fortran and used in commercial software (ABAQUS) for numerical simulation. To study the effect of damage extension of materials on post-impact and post-impact compression for different hygrothermal times. It was found that the residual compressive strength depended on factors such as the material's hygrothermal time and the initial defects in the plywood; that the 90° and ± 45° fibre orientations played a positive role in the material's hygrothermal; that the hygrothermal made the material's damage more catastrophic; and that the buckling of hygrothermal specimens was not only at the impact position, but was also reflected at the edges. In CAI testing, it was found that the hygrothermally treated specimens were damaged similarly to the desiccation treated specimens, but that compression resulted in a flexural position affected by hygrothermal, which determined the material CAI strength.

Investigation of the hygrothermal effects on in-plane failure mechanisms of fine Z-pinned laminates

Effect of Ø 0.11 Mm Z-pinning on the Properties of Composite Laminates Via an Ultrasound Guided Insertion Process

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Micro-damage Initiation Evaluation of Z-Pinned Laminates Based on a New Three-Dimension RVE Model

Strengthening of Composite T-joints Using Ø 0.11 Mm Z-pins Via an Ultrasound-Guided Insertion Process

Minimizing the In-Plane Damage of Z-pinned Composite Laminates Via a Pre-Hole Pin Insertion Process

Experimental Investigation of Z-pin Insertion Angles on the Mechanical Behavior and Failure Mechanism of Compression after Impact for CFRP Laminates

Effect of Z-pin Insertion Angles on Low-Velocity Impact Mechanical Response and Damage Mechanism of CFRP Laminates with Different Layups

Out-of-plane Properties and Failure Mechanism of Composite Laminates Reinforced with Carbon Z-pins

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Effect of fine metallic Z-pin on compressive property of open-hole composite laminate

Fatigue life assessment and damage evolution in Z-pinned laminates

Influence of Z‐pin material on the mechanical properties of fine Z‐pin reinforced composites

Balance Interlaminar Improvement and In-Plane Adverse Impact of Hexagonal Semi-Embedded Fine Z-pin Reinforced Polymer Composite

Effect of Z-pin inclined angle on the impact damage suppression effectiveness for cross-ply composite laminates

Enhancement of Composite Open-Hole Tensile Strength Via Fine Z-pins Arrangements

Using z-pinning to improve the low-velocity impact performance of composite skin/stringer structures

Analysis of Residual Post-Impact Compressive Strength of Composite Laminates Under Hygrothermal Conditions

Experimental investigations into damage mechanism in the low‐velocity impact and tension‐after‐impact testing of z‐pin reinforced curved CFRP composite

Low‐velocity impact resistance of the Z‐pin reinforced carbon fiber composite laminates

Effect of Hygrothermal Aging on Compression Behavior of CFRP Material with Different Layups