Abstract:The microstructural evolution during homogenization of aluminum 6063 billet has been investigated in this work. DSC was used to observe thermal transition from room temperature to 600 °C. Three transition temperature ranges, 218-353, 381-473, and 498-581 °C, were observed. These temperature ranges were assigned as three transformation stages occurring during homogenization. The finish transformation temperatures were selected for conducting isothermal treatments. In the first transformation stage, plate-like intermetallics (β) became thinner and fine black particles consisting of Mg and Si precipitated within matrix leading to Mg depletion from the matrix. The 353 °C heat-treated specimen showed lowest hardness and room temperature tensile strength probably due to Mg deficiency for solid solution strengthening. The 473 °C heat-treated specimen showed low hardness and room temperature tensile strength. In the third stage (581 °C isothermal treatment), globular intermetallics (α) distributed all over the matrix and most fine black particles underwent dissolution. Mg was found to dissolve back to the matrix. The 581 °C heat-treated specimen showed the highest hardness and room temperature tensile strength among all heat-treated specimens. All isothermally heat-treated specimens were also subject to tensile test at 470 °C to understand their behavior at the pre-heating temperature of extrusion commonly used as industrial practice. It was found that the specimens showed the flow stresses from the highest to the lowest as follows: the as-cast, the isothermally treated at 353, 473, and 581 °C, respectively. The flow stresses at 470 °C depended on the morphology and distribution of intermetallics due to isothermal temperatures. The isothermal treatment at 581 °C, producing globular intermetallics (α) all over the grains and lowest flow stress, is recommended for homogenization of aluminum 6063 billets. Causes responsible for such microstructural changes and mechanical properties during the three stages are discussed in this study.

Influence of Homogenization Heat Treatment and Cooling Modes on Microstructure of AA7475 Aluminum Alloy Ingot

Microstructural Evolution and Kinetics of 7075 Al Alloy During Homogenization Treatment

Microstructural Characterization of the As-Cast and Homogenized Al-Cu-Mg-Ag Alloy

Homogenization heat treatment influence on microstructure evolution and mechanical properties of as-cast Al-Li-Cu-Mg-Zr alloy for lightweight aerospace application

Isothermal Investigation and Deformation Behavior during Homogenization of 6063 Aluminum Alloy

Effect of homogenization temperature on microstructural homogeneity and mechanical properties of twin-roll casted 8006 aluminum alloy

Homogenization heat treatment of Mg-9.0Y-3.0MM-0.6Zr alloy

Effect of Solution Heat Treatment on the Microstructure and Microhardness of 7050 Aluminum Alloy

High-Temperature Phase Transformations in Al-Li-Cu-Mg-Zr-Sc Alloy Studied via In Situ Electron Microscopy

Effect of Composition on Microstructural Evolution during Homogenization of 7XXX Alloys

Effects of Homogenization Treatment on the Microstructure and Mechanical Properties of Mg–8Li–3Al–Y Alloy

Research on Homogenization Treatment of Mg-8wt.% Sn-1.5 Wt.% Al Alloy

Effect of the Fe/Mn Ratio on the Microstructural Evolution of the AA6063 Alloy with Homogenization Heat Treatment Interruption

Modeling of Microsegregation and Homogenization of 6xxx Al-Alloys Including Precipitation and Strengthening During Homogenization Cooling

Tailoring intermetallic phase and mechanical property improvement in a novel Al-Zn-Mg-Cu-Y alloy via homogenization treatment

Intermetallic and dispersoid structures in AA3104 aluminium alloy during two-step homogenisation

Homogenization Treatment of Mg?6Zn?3Sn (wt.％) Alloy and Its Effects on Microstructure and Mechanical Properties

Study on the inhomogeneity of Al–Zn–Cu–Mg aluminum alloy plates with different thickness

Elevated Temperature Mechanical Property Degradation of AA7475 Aluminum Alloy: In Situ Microstructure Analysis

Homogenization heat treatment of GWN751K magnesium alloy

Effect of heat treatment on the microstructure and mechanical properties of Al‐9Si‐0.4Mg‐0.1Cu alloy