Microstructural Evolution and Kinetics of 7075 Al Alloy During Homogenization Treatment
Yang Ding,Tao He,Jun-jie Zhang,Xiang-yang Du,Alexey Vereschaka
DOI: https://doi.org/10.1007/s11837-024-06994-5
2024-11-23
JOM
Abstract:Homogenization treatment reduces elemental microsegregation and promotes homogeneous solute distribution, thereby enhancing microstructural homogeneity and mechanical properties. This study employed optical microscopy, scanning electron microscopy, energy-dispersive spectroscopy and Vickers microhardness tester to systematically investigate the microstructural evolution, compositional distribution and microhardness of as-cast 7075 Al alloy during homogenization. Significant dendritic microsegregation was observed in the as-cast alloy, particularly with Cu, Mg and Zn concentrated along grain boundaries and dendritic cores. As homogenization temperature and holding times increased, dendritic structures gradually diminished, and non-equilibrium phases dissolved into the matrix. At 465°C for 24 h, the second-phase area decreased from 6.67% to 1.58%, and the grain boundary width reduced from 4.47 μm to 2.29 μm. After further homogenization at 475°C for 4 h, the grain boundary width is approximately 0.68 μm, and the area fraction of the second phase is only 0.65%. Initially, the dissolution of low-melting non-equilibrium phases decreases microhardness. Longer homogenization and cooling processes cause phase transformations, slightly increasing and stabilizing hardness. The optimal double-stage homogenization treatment achieved a homogeneous microstructure. Diffusion kinetics during homogenization revealed that the redistribution of alloying elements, driven by atomic diffusion, effectively reduces elemental microsegregation and optimizes processing parameters.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy