Microstructural evolution and mechanical properties of cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc alloys during heat treatment

Zepeng Zha,Zhenqiang Wang,Zelin Wu,Dongshen Huo,Shuai Zhang,Chunhong Zhang,Yunpeng Chang,Chao Xu,Fengchun Jiang
DOI: https://doi.org/10.1002/adem.202400643
IF: 3.6
2024-06-11
Advanced Engineering Materials
Abstract:Cu is commonly used to improve the mechanical properties of Al‐Li alloys, but its exact role in multicomponent Al‐Li alloys is not fully understood. In this paper, the microstructure and mechanical properties of two cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc (wt.%) alloys aged at 165°C are compared. The results show that Alloy 1.4Cu possesses finer grain size and better mechanical properties than Alloy 0.5Cu. The δ′ (Al3Li), Al3(Sc, Zr, Li) phases and Guinier–Preston–Bagaryatsky (GPB) zones were formed in both alloys. During the early stage of ageing (8h), many dispersed S′ (Al2CuMg) phases precipitated only in Alloy 1.4Cu and coarsened continuously. Instead, many rod‐shaped S1 (Al2MgLi) phases started to precipitate in Alloy 0.5Cu up to ageing for 32h and then coarsened continuously with ageing. Moreover, Alloy 1.4Cu showed narrower δ′‐Precipitate Free Zones (δ′‐PFZs) along grain boundaries than Alloy 0.5Cu. The higher strength and ductility with more uniform strain distribution for Alloy 1.4Cu than Alloy 0.5Cu is attributed to finer grain size and unique phase formation for the former. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary
What problem does this paper attempt to address?