Effect of the Fe/Mn Ratio on the Microstructural Evolution of the AA6063 Alloy with Homogenization Heat Treatment Interruption

Adolfo Galván Avalos,Jesús Torres Torres,Alfredo Flores Valdés
DOI: https://doi.org/10.3390/met14040373
IF: 2.695
2024-03-24
Metals
Abstract:The casting structure of the AA6063 alloy contains intermetallic particles of β-Al5FeSi, which can result in the fragility of the cast pieces. However, with heat treatment, the β phase transforms from a needle or plate form into an intermetallic phase known as α, which resembles Chinese-script in its morphology. To analyze the effect of the ratio of Fe/Mn with different ratios of 0.5, 0.75, and 1, a heat treatment process is used with intermittent interruptions. The alloy is subjected to a temperature of 575 °C for 12 h to determine the microstructural evolution of the β-Al6FeMn and α-Al15(FeMn)3Si2 phases. This study used scanning electron microscopy to conduct point analyses and elemental mappings of the intermetallics found in the casting and heat treatment samples. Additionally, X-ray diffraction was employed to determine the stoichiometry of the present phases. The results indicated that the cast structure contains β-Al6FeMn and α-Al15(FeMn)3Si2 phases and that the β-Al6FeMn phase transforms into the α-Al15(FeMn)3Si2 phase upon completion of the heat treatment process. By using specific Fe/Mn ratios, the formation of the needle-shaped Al5FeSi phase in the casting structure of the alloy can be inhibited, leading to the precipitation of phases such as β-Al6FeMn and α-Al15(FeMn)3Si2 instead.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to analyze the influence of the Fe/Mn ratio on the microstructure evolution of AA6063 aluminum alloy during the interruption of homogenization heat treatment. Specifically, the research focuses on the following points: 1. **Influence of Fe/Mn ratio on the phase transformation of β - Al6FeMn and α - Al15(FeMn)3Si2**: By controlling the Fe/Mn ratio (0.5, 0.75 and 1 respectively), observe how these ratios affect the transformation process from β - Al6FeMn phase to α - Al15(FeMn)3Si2 phase. 2. **Microstructure changes during heat treatment**: Study the changes of the microstructure of AA6063 alloy over time when it is heat - treated at 575°C for 12 hours under different Fe/Mn ratios. Samples are taken every 30 minutes during the heat treatment process until the total time reaches 660 minutes. 3. **Inhibition of the formation of acicular Al5FeSi phase**: By adjusting the Fe/Mn ratio, inhibit the formation of the harmful acicular Al5FeSi phase formed during the casting process, and promote the precipitation of β - Al6FeMn and α - Al15(FeMn)3Si2 phases which are more beneficial to mechanical properties. ### Research background AA6063 aluminum alloy is widely used in the transportation industry, such as automobile chassis frames and battery module housings. However, a high Fe content will lead to the formation of acicular β - Al5FeSi phase, which will reduce the mechanical properties of the alloy, such as ductility and fatigue strength. Therefore, optimizing the microstructure through heat treatment and adjusting the Fe/Mn ratio is crucial for improving the quality of the alloy. ### Research methods - **Material preparation**: Manufacture pre - forms using raw materials with different Fe/Mn ratios. - **Heat treatment**: Conduct a 12 - hour homogenization heat treatment at 575°C, and take samples every 30 minutes. - **Microstructure analysis**: Use scanning electron microscopy (SEM) and X - ray diffraction (XRD) to analyze the microstructure and phase composition of the samples. - **Quantitative analysis**: Quantify the area percentages of β and α phases through image analysis software (Image - Pro 6.0). ### Results and discussion The research results show that as the heat treatment time prolongs, the β - Al6FeMn phase gradually transforms into the α - Al15(FeMn)3Si2 phase. In particular, when the Fe/Mn ratio is 0.5, a complete transformation from β to α is achieved within 540 minutes. In contrast, for samples with Fe/Mn ratios of 1 and 0.75, a small amount of β phase still exists after 660 minutes. In addition, the research also found that a higher manganese content promotes the formation of the α - Al15(FeMn)3Si2 phase, and this phase has a Chinese calligraphy - like morphology, which helps to improve the mechanical properties of the alloy. ### Conclusion This research shows that by adjusting the Fe/Mn ratio, the microstructure evolution of AA6063 aluminum alloy during heat treatment can be effectively controlled, especially the formation of the harmful acicular Al5FeSi phase can be inhibited, thereby improving the mechanical properties and quality of the alloy.