Abstract:A high Fe content easily produces Fe-rich phases with a harmful morphology, resulting in a huge detrimental effect on the properties and recycling ability of Al-Si alloys. Therefore, finding ways to effectively transform Fe-rich phases to form a beneficial phase or shape is of great significance. Accordingly, Al-Si-based alloys with Fe contents ranging from 0.1 wt.% to 2.0 wt.% were modified by different Mn additions. Moreover, experiments combined with simulations were utilized to comprehensively analyze the mechanism of Mn on the morphology and microstructural evolution of Fe-rich phases from different perspectives. The current findings determine that adding different Fe contents changes the phase-transition reactions in alloys. Without Mn, and by increasing the Fe content from 0.1 wt.% to 2.0 wt.%, the Fe-rich phases gradually convert from a skeleton-shaped α-Al8Fe2Si (<0.25 wt.%) to β-Al9Fe2Si2 with a fibrous (0.5 wt.%), needle-like (1.0 wt.%) and plate-like shape without curvatures (2.0 wt.%). The maximum length and mean aspect ratio increase from 12.01 μm to 655.66 μm and from 1.96 to 84.05, while the mean curvature decreases from 8.66 × 10−2 μm−1 to 8.25 × 10−4 μm−1. The addition of 0.35 wt.% Mn promotes a new Chinese-character and petal-shaped α-Al15(FeMn)3Si2, with an atomic ratio of Fe and Mn of 1:1 when the Fe content is lower than 0.5 wt.%, while it transforms to β-Al15(FeMn)3Si2 with an atomic ratio of 5:1, presenting as a refined plate-like shape with a certain curvature, as the Fe content increases to 2.0 wt.%. Mn alters the phase reactions and increases the threshold of the Fe content required for β-Al15(FeMn)3Si2, limiting the formation and growth of them simultaneously in time and space. The enrichment of Mn atoms and solute diffusion at the growth front of β-Al15(FeMn)3Si2, as well as the strong atomic-binding ability, can deflect the growth direction of β-Al15(FeMn)3Si2 for it to have a certain curvature. Additionally, the enriched Mn atoms easily form α-Al15(FeMn)3Si2 and cause the long β-Al15(FeMn)3Si2 to be broken and refined to further reduce the damages caused to the alloy's performance. Ultimately, the maximum length and mean aspect ratio can be effectively reduced to 46.2% and 42.0%, respectively, while the mean curvature can be noticeably increased by 3.27 times with the addition of Mn.

Formation of intermetallic phases during solidification in Al-Mg-Mn 5xxx alloys with various Mg levels

Formation of Phases and Microstructures in Al-8Si Alloys with Different Mg Content

The Effect of Mn on the Microstructure of Spray-Deposited Al–20Si–5Fe–3Cu–1Mg Alloy

Influence of the Mg Content on the Microstructure and Mechanical Properties of Al-xMg-2.0Si-0.6Mn Alloy

Effect of Fe and Mn Content on the Microstructures and Tensile Behaviour of AlSi7Cu3 Alloy: Thermal Analysis and Tensile Tests

Morphology, thermal stability, electronic structure and mechanical properties of α-AlFeMnSi phases with varying Mn/Fe atomic ratios: Experimental studies and DFT calculations

Alloying effect of Mg on microstructure and mechanical properties at 300 °C of Al–5Cu–1Mn–0.5Ni heat-resistant alloy

Effect of Cu and Mn content on solidification microstructure, T-phase formation and mechanical property of Al Cu Mn alloys

Microstructure Evolution and Corresponding Mechanism of Al–Si–Mg–Cu Alloy with Addition of Mn/Mn+Cr

Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents

Iron Intermetallic Phases in the Alloy Based on Al-Si-Mg by Applying Manganese

Phases Formation and Evolution at Elevated Temperatures of Al–12Si–3.8Cu–2Ni–1Mg Alloy†

The influence of cooling rate and manganese content on the β-Al5FeSi phase formation and mechanical properties of Al–Si-based alloys

Influences of Mg content on the microstructures and mechanical properties of cast Al–2Li–2Cu–0.2Zr alloy

Influence of Si Addition on the Microstructure and Mechanical Behaviour of Mg-5Sn-3Zn-1Mn Alloy

Study of the evolution mechanisms of Fe-rich phases in Al-Si-Fe alloys with Mn modification using synchrotron X-ray imaging

On the Sc induced solidification-heterogeneous microstructure in selective laser melted Al-5Mn alloys

Effect of Zn/Mg ratio on the microstructure and mechanical properties of as-cast Al–Zn–Mg–Cu alloys and the phase transformation during homogenization

Optimizing the Morphology and Solidification Behavior of Fe-Rich Phases in Eutectic Al-Si-Based Alloys with Different Fe Contents by Adding Mn Elements

Solidification Microstructure and Mechanical Properties of Cast Magnesium-Aluminum-Tin Alloys

Cooperative Effect of Mg and Si Contents on the Microstructural Evolution, Mechanical Performance, and Deformation Behavior of Cast Al–Li–Mg–Si Alloys