Effect of Addition of Rare Earth Elements on the Microstructure, Texture, and Mechanical Properties of Extruded ZK60 Alloy

DOI: https://doi.org/10.1007/s12540-022-01341-2

IF: 3.451

2022-11-25

Metals and Materials International

Abstract:Microstructure, texture and mechanical properties of extruded ZK60 alloys containing different rare earth (RE) elements were studied. Two alloys containing 1 and 2 wt% Ce-rich lanthanides as well as two other alloys with 1 and 2 wt% Y were prepared and denoted as ZK60–1RE, ZK60–2RE, ZK60–1Y and ZK60–2Y, respectively. The results showed that the addition of RE elements refined the grain size of the ZK60 alloy, and Y had a more significant effect on the grain size reduction. The finer grain size in the ZK60–1Y and ZK60–2Y alloys (2.3 and 2.1 μm, respectively) compared to ZK60–1RE and ZK60–2RE alloys (6.2 and 3.7 μm, respectively) was attributed to the pinning effect of very fine secondary phases on grain boundaries. While the ZK60–1Y alloy exhibited a fiber texture with a slight rotation of < > poles around the extrusion direction, the ZK60–1RE alloy showed a new texture component known as RE texture. Moreover, there were no changes in the fiber-like texture component of ZK60–2RE and ZK60–2Y alloys. The mechanical properties of the alloys were assessed by shear punch test. Accordingly, the addition of RE and Y elements enhanced the shear strength, and the maximum ultimate shear strength of 176 MPa was obtained for the ZK60–2RE alloy. The higher dislocation density, the lower volume fraction of dynamically recrystallized regions compared to other alloys, and the large fraction of secondary phase particles were responsible for this high strength value. Graphical

materials science, multidisciplinary,metallurgy & metallurgical engineering