Abstract:Mg–6.0 Zn–2.0 Yb–0.5 Zr (wt.%) alloy exhibits excellent strength and ductility synergy after thermomechanical and heat treatment. Unfortunately, the hot workability and microstructure evolution under specific deformation regimes remain uncertain to date. In this work, the constitutive model and hot processing maps were established based on a series of isothermal compression tests. A detailed examination of deformation microstructures at different processing regimes revealed that the hot workability and correlated microstructure development were deformation condition dependent. When compressed at lower strain rates and higher deformation temperatures, the softening was promoted by dynamic recrystallization (DRX) and the prevalence of discontinuous dynamic recrystallization (DDRX) generally resulted in a complete DRX process with coarse grains and much-intensified texture. On the contrary, work hardening was improved with increasing dislocation density, and the continuous DRX (CDRX) may control the partial DRX progress, often presenting a much-refined microstructure with a more dispersed texture. Interestingly, a low strain rate of 0.001 s −1 and a moderate deformation temperature of 300 °C effectively balanced the nucleation rate and grain growth to finally achieve a much refined and relatively homogeneous grain structure. Further investigation concerning the activation energy suggested that the workability improved with increasing strain rate and temperature. Enhanced hot workability at most deformation regimes was achieved due to a lower average activation energy Q value in comparison with that of 1.0 wt.% Yb alloyed ZK60 counterpart, which was likely due to a higher activity of non-basal slips achieved in this alloy.

Processing Maps and Hot Compression Behaviors of ZK60 Alloy After Adding Different Rare Earth Elements

Effect of Rare Earth Elements on the Microstructural and Mechanical Properties of ZK60 Alloy after T5 Treatment

Modification of the Tensile Performance of an Extruded ZK60 Magnesium Alloy with the Addition of Rare Earth Elements

Processing maps for hot working of ZK60 magnesium alloy

Effect of Addition of Rare Earth Elements on the Microstructure, Texture, and Mechanical Properties of Extruded ZK60 Alloy

Hot Deformation and Processing Maps of Al18B4O33w/ZK60 Composite

Characterization of hot deformation behavior of extruded ZK60 magnesium alloy using 3D processing maps

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Processing maps of extruded AZ80 + 0.4% Ce magnesium alloy

Hot workability and microstructure of Mg–6.0 Zn–2.0 Yb–0.5 Zr magnesium alloy

Microstructure and mechanical properties of extruded ZK60 magnesium alloy containing rare earth

Hot Compression Deformation Behavior and Processing Maps of Mg-Gd-Y-Zr Alloy

Hot Deformation Behavior and Workability of Pre-Extruded ZK60A Magnesium Alloy

Hot Workfability Behavior of As-Cast Mg–Zn–Y–Zr Alloy

Effect of adding Y and Ce on corrosion behaviour of the extruded ZK60 magnesium alloy

Hot deformation behavior of an extruded AZ31 alloy doped with rare-earth elements

Influence of Cyclic Extrusion and Compression on the Mechanical Property of Mg Alloy Zk60

Hot Deformation Behavior and Processing Map of Coarse-Grained Mg–Gd–Y–Nd–Zr Alloy

Hot Deformation Behavior, Processing Maps and Microstructural Evolution of the Mg-2.5Nd-0.5Zn-0.5Zr Alloy

Effect of Zr and Er Addition on the Microstructural Evolution of a Novel Al−Mg−Zn−Er−Zr Alloy during Hot Compression

Hot Deformation Behavior and Processing Map of Squeeze Cast Zk60 Magnesium Alloy