Hot workability and microstructure of Mg–6.0 Zn–2.0 Yb–0.5 Zr magnesium alloy

Chunrong Liu,Lu Li,Wei Zhou,Xue Bai,Huiling Zhong,Ziqi Zhang,Zhuozhang Wen

DOI: https://doi.org/10.1016/j.jallcom.2022.168356

IF: 6.2

2022-12-07

Journal of Alloys and Compounds

Abstract:Mg–6.0 Zn–2.0 Yb–0.5 Zr (wt.%) alloy exhibits excellent strength and ductility synergy after thermomechanical and heat treatment. Unfortunately, the hot workability and microstructure evolution under specific deformation regimes remain uncertain to date. In this work, the constitutive model and hot processing maps were established based on a series of isothermal compression tests. A detailed examination of deformation microstructures at different processing regimes revealed that the hot workability and correlated microstructure development were deformation condition dependent. When compressed at lower strain rates and higher deformation temperatures, the softening was promoted by dynamic recrystallization (DRX) and the prevalence of discontinuous dynamic recrystallization (DDRX) generally resulted in a complete DRX process with coarse grains and much-intensified texture. On the contrary, work hardening was improved with increasing dislocation density, and the continuous DRX (CDRX) may control the partial DRX progress, often presenting a much-refined microstructure with a more dispersed texture. Interestingly, a low strain rate of 0.001 s −1 and a moderate deformation temperature of 300 °C effectively balanced the nucleation rate and grain growth to finally achieve a much refined and relatively homogeneous grain structure. Further investigation concerning the activation energy suggested that the workability improved with increasing strain rate and temperature. Enhanced hot workability at most deformation regimes was achieved due to a lower average activation energy Q value in comparison with that of 1.0 wt.% Yb alloyed ZK60 counterpart, which was likely due to a higher activity of non-basal slips achieved in this alloy.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering